BS 970 (Part 1) 832H13 vs EN 10084 14NiCrMo13-4

Close Alternative — 76.9% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 832H13 (BS 970 (Part 1):1983) and EN 10084 14NiCrMo13-4 (EN 10084:2008) are both steel grades. Both fall under the Alloy Steel category. BS 970 (Part 1) 832H13 is typically used for case hardening steel supplied to specified hardenability limits (end quench test, table 10)., while EN 10084 14NiCrMo13-4 is commonly used for case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1). BS 970 (Part 1) 832H13 is defined under British Standards (BS), originating from United Kingdom, while EN 10084 14NiCrMo13-4 is defined under European Standard (EN), originating from Europe.

As per chemical composition, BS 970 (Part 1) 832H13 vs EN 10084 14NiCrMo13-4 is a 76.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.9%.

Frequently Compared With BS 970 (Part 1) 832H13:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 NF A35-565 100C6 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H UNI 11234 100Cr6
Match Breakdown
CHEMISTRY MATCH
76.9%
MECHANICAL MATCH
No shared data
OVERALL
76.9%
Specifications
Property BS 970 (Part 1) 832H13 EN 10084 14NiCrMo13-4
Standard BS 970 (Part 1):1983 EN 10084:2008
Category Alloy Steel Alloy Steel
C (%) 0.10-0.16 0.11-0.17
Mn (%) 0.35-0.60 0.30-0.60
Cr (%) 0.70-1.00 0.80-1.10
Mo (%) 0.10-0.25 0.20-0.30
Ni (%) 3.00-3.75 3.00-3.50
P (%) <=0.035 <=0.025
S (%) <=0.040 <=0.035
Si (%) Not specified <=0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 832H13 EN 10084 14NiCrMo13-4
Condition Not specified Soft annealed
Hardenability Not specified +H band at 1.5 mm from the quenched end: 39 to 47 HRC
Hardness Not specified Soft annealed: 241 HB max
Typical Applications
BS 970 (Part 1) 832H13
Case hardening steel supplied to specified hardenability limits (end quench test, Table 10).
EN 10084 14NiCrMo13-4
Case hardened machine parts: carburized or carbonitrided, then hardened (clause 3.1)
Key Differences
Can BS 970 (Part 1) 832H13 Be Substituted With EN 10084 14NiCrMo13-4?
BS 970 (Part 1) 832H13 and EN 10084 14NiCrMo13-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
BS 970 (Part 1) 832H13
0 active listings and RFQs →
EN 10084 14NiCrMo13-4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 832H13 and EN 10084 14NiCrMo13-4?
EN 10084 14NiCrMo13-4 specifies Si which is not specified for BS 970 (Part 1) 832H13.
Can BS 970 (Part 1) 832H13 be substituted with EN 10084 14NiCrMo13-4?
BS 970 (Part 1) 832H13 and EN 10084 14NiCrMo13-4 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.