BS 970 (Part 1) 316S13 vs GB/T 3280 06Cr19Ni10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

BS 970 (Part 1) 316S13 (BS 970 (Part 1):1991) and GB/T 3280 06Cr19Ni10 (GB/T 3280-2015) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 1) 316S13 is typically used for austenitic stainless and heat resisting steel (section five), while GB/T 3280 06Cr19Ni10 is commonly used for used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.. BS 970 (Part 1) 316S13 is defined under British Standards (BS), originating from United Kingdom, while GB/T 3280 06Cr19Ni10 is defined under Guobiao Standards (GB/T), originating from China.

As per chemical composition, BS 970 (Part 1) 316S13 vs GB/T 3280 06Cr19Ni10 is a 71% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With BS 970 (Part 1) 316S13:
EN 10088-1 1.4301 EN 10088-1 1.4401 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
71%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property BS 970 (Part 1) 316S13 GB/T 3280 06Cr19Ni10
Standard BS 970 (Part 1):1991 GB/T 3280-2015
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08 max
Si (%) <=1.0 1.00 max
Mn (%) <=2.0 2.00 max
P (%) <=0.045 0.045 max
S (%) <=0.030 0.030 max
Cr (%) 16.5-18.5 18.00-20.00
Mo (%) 2.50-3.00 Not specified
Ni (%) 11.5-14.5 8.00-11.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 1) 316S13 GB/T 3280 06Cr19Ni10
Condition Softened, 1000-1100 deg C Not specified
Tensile Strength 490 MPa min 520-720 MPa
Yield Strength 190 MPa min (0.2% proof) 205-310 MPa
Elongation 40 % min 40-60%
Hardness 183 HB max 187 HB max
Typical Applications
BS 970 (Part 1) 316S13
Austenitic stainless and heat resisting steel (section five)
GB/T 3280 06Cr19Ni10
Used for kitchen equipment, food processing machinery, chemical tanks, piping, architectural panels, and fasteners.
Key Differences
Can BS 970 (Part 1) 316S13 Be Substituted With GB/T 3280 06Cr19Ni10?
BS 970 (Part 1) 316S13 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
BS 970 (Part 1) 316S13
No active listings currently.
GB/T 3280 06Cr19Ni10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2900–3300 mm (114.17–129.92 in)
On M-EX Right Now
BS 970 (Part 1) 316S13
0 active listings and RFQs →
GB/T 3280 06Cr19Ni10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 1) 316S13 and GB/T 3280 06Cr19Ni10?
BS 970 (Part 1) 316S13 specifies Mo which is not specified for GB/T 3280 06Cr19Ni10.
Can BS 970 (Part 1) 316S13 be substituted with GB/T 3280 06Cr19Ni10?
BS 970 (Part 1) 316S13 and GB/T 3280 06Cr19Ni10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.