BS 970 EN2E vs IS 11169 (Part 1) 7C4

Strong Match — 95% match based on chemical composition and mechanical property overlap.

BS 970 EN2E (BS 970:1955) and IS 11169 (Part 1) 7C4 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Carbon Steel category. BS 970 EN2E is typically used for bars and billets for forging; forgings and drop-forgings; bars for machining, while IS 11169 (Part 1) 7C4 is commonly used for cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1). BS 970 EN2E is defined under British Standards (BS), originating from United Kingdom, while IS 11169 (Part 1) 7C4 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 EN2E vs IS 11169 (Part 1) 7C4 is a 92.6% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 95%.

Frequently Compared With BS 970 EN2E:
BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 060A45 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
92.6%
MECHANICAL MATCH
100%
OVERALL
95%
Specifications
Property BS 970 EN2E IS 11169 (Part 1) 7C4
Standard BS 970:1955 IS 11169 (Part 1):1984
Category Carbon Steel Carbon Steel
C (%) <=0.15 <=0.12
Si (%) 0.10-0.35 Not specified
Mn (%) <=0.50 <=0.50
S (%) <=0.050 Not specified
P (%) <=0.050 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 EN2E IS 11169 (Part 1) 7C4
Tensile Strength ≥309 MPa (20 tons/sq in, converted) Not specified
Elongation ≥28% Not specified
Hardness ≤120 HB Not specified
Condition , ruling section 6 in (lowest-strength condition of the standard) Not specified
Hardness, annealed Not specified <=120 HB
Typical Applications
BS 970 EN2E
Bars and billets for forging; forgings and drop-forgings; bars for machining
IS 11169 (Part 1) 7C4
Cold heading and cold extrusion; the standard covers wires, wire rods and bars of 2 to 100 mm diameter (clause 1.1)
Key Differences
Can BS 970 EN2E Be Substituted With IS 11169 (Part 1) 7C4?
BS 970 EN2E and IS 11169 (Part 1) 7C4 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 7C4 is often considered as a substitute for BS 970 EN2E in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 EN2E
0 active listings and RFQs →
IS 11169 (Part 1) 7C4
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 EN2E and IS 11169 (Part 1) 7C4?
BS 970 EN2E specifies Si, S, P which are not specified for IS 11169 (Part 1) 7C4.
Can BS 970 EN2E be substituted with IS 11169 (Part 1) 7C4?
BS 970 EN2E and IS 11169 (Part 1) 7C4 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 7C4 is often considered as a substitute for BS 970 EN2E in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.