BS 970 (Part 3) 316S33 vs IS 1570 (Part 5) X04Cr17Ni12Mo2

Strong Match — 89.4% match based on chemical composition and mechanical property overlap.

BS 970 (Part 3) 316S33 (BS 970 (Part 3):1991) and IS 1570 (Part 5) X04Cr17Ni12Mo2 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. BS 970 (Part 3) 316S33 is defined under British Standards (BS), originating from United Kingdom, while IS 1570 (Part 5) X04Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, BS 970 (Part 3) 316S33 vs IS 1570 (Part 5) X04Cr17Ni12Mo2 is a 89.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 89.4%.

Frequently Compared With BS 970 (Part 3) 316S33:
IS 1570 (Part 7) 12Cr12MoH ASTM A959 .- GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
89.4%
MECHANICAL MATCH
No shared data
OVERALL
89.4%
Specifications
Property BS 970 (Part 3) 316S33 IS 1570 (Part 5) X04Cr17Ni12Mo2
Standard BS 970 (Part 3):1991 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.07 <=0.08
Si (%) <=1.0 <=1.0
Mn (%) <=2.0 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 16.5-18.5 16.0-18.0
Mo (%) 2.50-3.00 2.0-3.0
Ni (%) 11.0-14.0 10.0-14.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property BS 970 (Part 3) 316S33 IS 1570 (Part 5) X04Cr17Ni12Mo2
Tensile Strength Not specified >=515 MPa
Yield Strength Not specified >=205 MPa (0.2 % proof stress)
Elongation Not specified >=40% (50 mm)
Hardness Not specified <=217 HB; <=95 HRB
Condition Not specified Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Typical Applications
BS 970 (Part 3) 316S33
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; austenitic stainless and heat resisting steel (Table 18)
IS 1570 (Part 5) X04Cr17Ni12Mo2
Not documented
Can BS 970 (Part 3) 316S33 Be Substituted With IS 1570 (Part 5) X04Cr17Ni12Mo2?
BS 970 (Part 3) 316S33 and IS 1570 (Part 5) X04Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr17Ni12Mo2 is often considered as a substitute for BS 970 (Part 3) 316S33 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
BS 970 (Part 3) 316S33
0 active listings and RFQs →
IS 1570 (Part 5) X04Cr17Ni12Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between BS 970 (Part 3) 316S33 and IS 1570 (Part 5) X04Cr17Ni12Mo2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can BS 970 (Part 3) 316S33 be substituted with IS 1570 (Part 5) X04Cr17Ni12Mo2?
BS 970 (Part 3) 316S33 and IS 1570 (Part 5) X04Cr17Ni12Mo2 overlap closely enough on chemistry and mechanical properties that IS 1570 (Part 5) X04Cr17Ni12Mo2 is often considered as a substitute for BS 970 (Part 3) 316S33 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.