Close Alternative — 71.3% match based on chemical composition and mechanical property overlap.

EN 10025-2 S355J0 (EN 10025-2:2019) and AS/NZS 3679.1 350 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S355J0 is typically used for hot rolled products of structural steels, while AS/NZS 3679.1 350 is commonly used for hot-rolled structural bars and sections for primary structural beams, columns, and framing. EN 10025-2 S355J0 is defined under European Standard (EN), originating from Europe, while AS/NZS 3679.1 350 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, EN 10025-2 S355J0 vs AS/NZS 3679.1 350 is a 92.2% match. As per mechanical properties, the match is 29.4%. Combined, this makes them a close alternative overall at 71.3%.

Frequently Compared With EN 10025-2 S355J0:
AS/NZS 3679.1 300 CSA G40.21 400W CSA G40.21 480W ASTM A1008 SS Grade 50
Other Structural Steel Grades to Compare With EN 10025-2 S355J0:
GOST 19281 09G2S CSA G40.21 260W CSA G40.21 300W CSA G40.21 350W CSA G40.21 400A ASTM A1008 SS Grade 80 ASTM A283C ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
92.2%
MECHANICAL MATCH
29.4%
OVERALL
71.3%
Specifications
Property EN 10025-2 S355J0 AS/NZS 3679.1 350
Standard EN 10025-2:2019 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) <=0.24 <=0.22
Si (%) <=0.55 <=0.50
Mn (%) <=1.60 <=1.70
P (%) <=0.030 <=0.040
S (%) <=0.030 <=0.040
N (%) <=0.012 Not specified
Cu (%) <=0.55 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S355J0 AS/NZS 3679.1 350
Tensile Strength 470-630 MPa 480-640 MPa
Yield Strength >=355 MPa 350 MPa min
Elongation >=22% 20% min
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Typical Applications
EN 10025-2 S355J0
Hot rolled products of structural steels
AS/NZS 3679.1 350
Hot-rolled structural bars and sections for primary structural beams, columns, and framing
Key Differences
Can EN 10025-2 S355J0 Be Substituted With AS/NZS 3679.1 350?
EN 10025-2 S355J0 and AS/NZS 3679.1 350 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
EN 10025-2 S355J0
No active listings currently.
AS/NZS 3679.1 350
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3200 mm (114.17–125.98 in)
On M-EX Right Now
EN 10025-2 S355J0
0 active listings and RFQs →
AS/NZS 3679.1 350
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S355J0 and AS/NZS 3679.1 350?
EN 10025-2 S355J0 specifies N, Cu which are not specified for AS/NZS 3679.1 350.
Can EN 10025-2 S355J0 be substituted with AS/NZS 3679.1 350?
EN 10025-2 S355J0 and AS/NZS 3679.1 350 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.