EN 10025-2 S235J2 vs AS/NZS 3679.1 300

Related Material — 61.3% match based on chemical composition and mechanical property overlap.

EN 10025-2 S235J2 (EN 10025-2:2019) and AS/NZS 3679.1 300 (AS/NZS 3679.1:2016) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S235J2 is typically used for used for bridges, structural sections, storage tanks, industrial buildings, transport frames, and support structures., while AS/NZS 3679.1 300 is commonly used for hot-rolled structural bars and sections for general structural framing. EN 10025-2 S235J2 is defined under European Standard (EN), originating from Europe, while AS/NZS 3679.1 300 is defined under Australian/New Zealand Standard (AS/NZS), originating from Australia/New Zealand.

As per chemical composition, EN 10025-2 S235J2 vs AS/NZS 3679.1 300 is a 87.2% match. As per mechanical properties, the match is 9.7%. Combined, this makes them a related material overall at 61.3%.

Frequently Compared With EN 10025-2 S235J2:
CSA G40.21 260W CSA G40.21 400W GOST 19281 09G2S CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 400A CSA G40.21 480W CSA G40.21 350W ASTM A1008 SS Grade 50 ASTM A283C ASTM A1008 SS Grade 80 ASTM A572 Gr.65
Match Breakdown
CHEMISTRY MATCH
87.2%
MECHANICAL MATCH
9.7%
OVERALL
61.3%
Specifications
Property EN 10025-2 S235J2 AS/NZS 3679.1 300
Standard EN 10025-2:2019 AS/NZS 3679.1:2016
Category Structural Steel Structural Steel
C (%) <=0.17 <=0.22
Mn (%) <=1.40 <=1.70
P (%) <=0.025 <=0.040
S (%) <=0.025 <=0.040
Cu (%) <=0.55 Not specified
Si (%) Not specified <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S235J2 AS/NZS 3679.1 300
Tensile Strength 360-510 MPa 440-600 MPa
Yield Strength >=235 MPa 300 MPa min
Elongation >=26% 22% min
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Typical Applications
EN 10025-2 S235J2
Used for bridges, structural sections, storage tanks, industrial buildings, transport frames, and support structures.
AS/NZS 3679.1 300
Hot-rolled structural bars and sections for general structural framing
Key Differences
Can EN 10025-2 S235J2 Be Substituted With AS/NZS 3679.1 300?
EN 10025-2 S235J2 and AS/NZS 3679.1 300 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-2 S235J2
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3400–4000 mm (133.86–157.48 in)
AS/NZS 3679.1 300
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2700–2700 mm (106.3–106.3 in)
On M-EX Right Now
EN 10025-2 S235J2
2 active listings and RFQs →
AS/NZS 3679.1 300
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S235J2 and AS/NZS 3679.1 300?
EN 10025-2 S235J2 specifies Cu which is not specified for AS/NZS 3679.1 300. AS/NZS 3679.1 300 specifies Si which is not specified for EN 10025-2 S235J2.
Can EN 10025-2 S235J2 be substituted with AS/NZS 3679.1 300?
EN 10025-2 S235J2 and AS/NZS 3679.1 300 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.