EN 10025-2:2019 S235JR Steel: Specifications & Listings
EN 10025-2:2019 S235JR: S235JR: non-alloy structural steel, hot rolled flat and long products, impact tested at 20 deg C (steel number 1.0038). Specified in EN 10025-2:2019.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Mn
P
S
N
Cu
<=0.17
<=1.40
<=0.035
<=0.035
<=0.012
<=0.55
Mechanical Properties
Tensile Strength
360-510 MPa
Yield Strength
>=235 MPa
Elongation
>=26%
Condition
Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces
Typical Available Sizes
Plate
5mm–100mm thk
Flat Bar
20×5mm–200×25mm
Angle
25×25×3mm–200×200×20mm
Sizes are indicative. Contact seller for exact availability.
More data from EN 10025-2:2019
From the standard
Yield strength by thickness9 thickness ranges
Thickness (mm)
Yield strength ReH, min (MPa)
up to 16
235
over 16 to 40
225
over 40 to 63
215
over 63 to 80
215
over 80 to 100
215
over 100 to 150
195
over 150 to 200
185
over 200 to 250
175
over 250 to 400
165
For plate, strip and wide flats of width 600 mm or more the transverse direction applies.
Source: EN 10025-2:2019, Table 6
Tensile strength by thickness5 thickness ranges
Thickness (mm)
Tensile strength Rm (MPa)
under 3
360 to 510
3 to 100
360 to 510
over 100 to 150
350 to 500
over 150 to 250
340 to 490
over 250 to 400
330 to 480
Source: EN 10025-2:2019, Table 6
Elongation by thickness6 thickness ranges
Thickness (mm)
Elongation A, longitudinal, min (%)
Elongation A, transverse, min (%)
3 to 40
26
24
over 40 to 63
25
23
over 63 to 100
24
22
over 100 to 150
22
22
over 150 to 250
21
21
over 250 to 400
21
21
Gauge length 5.65 times square root of cross-section area; values for thin products under 3 mm (gauge length 80 mm) not shown.
Source: EN 10025-2:2019, Table 6 (concluded)
Impact energy KV2, longitudinal3 thickness ranges
Thickness (mm)
Test temperature (deg C)
KV2 min (J)
up to 150
20
27
over 150 to 250
20
27
over 250 to 400
20
27
Longitudinal test pieces; subsized specimens reduced in proportion to area.
Source: EN 10025-2:2019, Table 8
Maximum carbon equivalent value (CEV)5 thickness ranges