EN 10025-2 S235JR vs CSA G40.21 480W

Related Material — 57.9% match based on chemical composition and mechanical property overlap.

EN 10025-2 S235JR (EN 10025-2:2019) and CSA G40.21 480W (CSA G40.21-13 (R2023)) are both steel grades. Both fall under the Structural Steel category. EN 10025-2 S235JR is typically used for structural fabrication, bridges, buildings, general engineering, while CSA G40.21 480W is commonly used for heavy cranes, offshore structures, high-rise building frames, pressure vessels, heavy mining equipment.. EN 10025-2 S235JR is defined under European Standard (EN), originating from Europe, while CSA G40.21 480W is defined under Canadian Standards Association (CSA), originating from Canada.

As per chemical composition, EN 10025-2 S235JR vs CSA G40.21 480W is a 86.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 57.9%.

Frequently Compared With EN 10025-2 S235JR:
ASTM A572 Gr.65 CSA G40.21 300W AS/NZS 3679.1 350 CSA G40.21 350W CSA G40.21 400A ASTM A283C GOST 19281 09G2S CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 400W ASTM A1008 SS Grade 50 ASTM A1008 SS Grade 80
Match Breakdown
CHEMISTRY MATCH
86.8%
MECHANICAL MATCH
0%
OVERALL
57.9%
Specifications
Property EN 10025-2 S235JR CSA G40.21 480W
Standard EN 10025-2:2019 CSA G40.21-13 (R2023)
Category Structural Steel Structural Steel
C (%) <=0.17 max 0.23
Mn (%) <=1.40 max 1.7
P (%) <=0.035 max 0.035
S (%) <=0.035 max 0.035
N (%) <=0.012 Not specified
Cu (%) <=0.55 Not specified
Si (%) Not specified max 0.5
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-2 S235JR CSA G40.21 480W
Tensile Strength 360-510 MPa 590-790 MPa
Yield Strength >=235 MPa 480 MPa min
Elongation >=26% Not specified
Condition Nominal thickness up to 16 mm (tensile for 3 to 100 mm, elongation for 3 to 40 mm), longitudinal test pieces Not specified
Typical Applications
EN 10025-2 S235JR
Structural fabrication, bridges, buildings, general engineering
CSA G40.21 480W
Heavy cranes, offshore structures, high-rise building frames, pressure vessels, heavy mining equipment.
Key Differences
Can EN 10025-2 S235JR Be Substituted With CSA G40.21 480W?
EN 10025-2 S235JR and CSA G40.21 480W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-2 S235JR
Plate → (3 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 3300–5100 mm (129.92–200.79 in)
CSA G40.21 480W
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3000 mm (114.17–118.11 in)
On M-EX Right Now
EN 10025-2 S235JR
3 active listings and RFQs →
CSA G40.21 480W
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-2 S235JR and CSA G40.21 480W?
EN 10025-2 S235JR specifies N, Cu which are not specified for CSA G40.21 480W. CSA G40.21 480W specifies Si which is not specified for EN 10025-2 S235JR.
Can EN 10025-2 S235JR be substituted with CSA G40.21 480W?
EN 10025-2 S235JR and CSA G40.21 480W share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.