EN 10025-3 S460 vs GOST 19281 09G2S

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10025-3 S460 (EN 10025-3:2019) and GOST 19281 09G2S (GOST 19281-2014) are both steel grades. Both fall under the Structural Steel category. EN 10025-3 S460 is typically used for used in structural frameworks, lifting equipment, pressure-support structures, transport chassis, and construction machinery., while GOST 19281 09G2S is commonly used for used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components.. EN 10025-3 S460 is defined under European Standard (EN) (Europe).

As per chemical composition, EN 10025-3 S460 vs GOST 19281 09G2S is a 61% match. As per mechanical properties, the match is 13.6%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10025-3 S460:
CSA G40.21 400A CSA G40.21 480W AS/NZS 3679.1 350 CSA G40.21 300W CSA G40.21 260W AS/NZS 3679.1 300 CSA G40.21 400W ASTM A1008 SS Grade 50 CSA G40.21 350W ASTM A572 Gr.65 ASTM A283C ASTM A1008 SS Grade 80
Match Breakdown
CHEMISTRY MATCH
61%
MECHANICAL MATCH
13.6%
OVERALL
35%
Specifications
Property EN 10025-3 S460 GOST 19281 09G2S
Standard EN 10025-3:2019 GOST 19281-2014
Category Structural Steel Structural Steel
C (%) 0.20 max 0.07-0.12
Si (%) 0.60 max 0.5-0.8
Mn (%) 1.70 max 1.3-1.7
P (%) 0.025 max 0.035 max
S (%) 0.020 max 0.04 max
Nb (%) 0.06 max Not specified
V (%) 0.12 max Not specified
Ti (%) 0.05 max Not specified
Ni (%) Not specified 0.3 max
Cr (%) Not specified 0.3 max
Cu (%) Not specified 0.3 max
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10025-3 S460 GOST 19281 09G2S
Tensile Strength 540-720 MPa 490-640 MPa
Yield Strength 460 MPa min 345 MPa min
Elongation 17% min 21% min
Hardness 180-230 HB 140-190 HB
Typical Applications
EN 10025-3 S460
Used in structural frameworks, lifting equipment, pressure-support structures, transport chassis, and construction machinery.
GOST 19281 09G2S
Used for bridges, pressure vessels, pipelines, structural frames, and heavy equipment components.
Key Differences
Can EN 10025-3 S460 Be Substituted With GOST 19281 09G2S?
EN 10025-3 S460 and GOST 19281 09G2S share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10025-3 S460
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2700–4400 mm (106.3–173.23 in)
GOST 19281 09G2S
Plate → (2 listings)
Thickness: 10–10 mm (0.39–0.39 in)
Width: 1500–1500 mm (59.06–59.06 in)
Length: 2900–3800 mm (114.17–149.61 in)
On M-EX Right Now
EN 10025-3 S460
2 active listings and RFQs →
GOST 19281 09G2S
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10025-3 S460 and GOST 19281 09G2S?
EN 10025-3 S460 specifies Nb, V, Ti which are not specified for GOST 19281 09G2S. GOST 19281 09G2S specifies Ni, Cr, Cu which are not specified for EN 10025-3 S460.
Can EN 10025-3 S460 be substituted with GOST 19281 09G2S?
EN 10025-3 S460 and GOST 19281 09G2S share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.