Close Alternative — 80.9% match
based on chemical composition and mechanical property overlap.
EN 10083-1 50CrMo4 (EN 10083-1:1991) and SAE J404 4150 (SAE J404:2000) are both steel grades.
Both fall under the Alloy Steel category.
EN 10083-1 50CrMo4 is typically used for quenched and tempered machine parts; non alloy steels also normalized (clause 1), while SAE J404 4150 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope.
EN 10083-1 50CrMo4 is defined under European Standard (EN), originating from Europe, while SAE J404 4150 is defined under SAE International, originating from United States.
As per chemical composition, EN 10083-1 50CrMo4 vs SAE J404 4150 is a 80.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 80.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10083-1 50CrMo4
SAE J404 4150
Condition
Quenched and tempered, ruling section d <= 16 mm
Not specified
Elongation
9% min
Not specified
Hardness
Soft annealed: 248 HB max
Not specified
Tensile Strength
1100 to 1300 MPa
Not specified
Yield Strength
900 MPa min
Not specified
Typical Applications
EN 10083-1 50CrMo4
Quenched and tempered machine parts; non alloy steels also normalized (clause 1)
SAE J404 4150
Chemistry-only alloy steel grade; see the composition notes for product scope
Can EN 10083-1 50CrMo4 Be Substituted With SAE J404 4150?
EN 10083-1 50CrMo4 and SAE J404 4150 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10083-1 50CrMo4 and SAE J404 4150?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10083-1 50CrMo4 be substituted with SAE J404 4150?
EN 10083-1 50CrMo4 and SAE J404 4150 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.