EN 10088-1 X2CrNiMnMoCuN24-4-3-2 vs ASTM A276/A276M S82441

Strong Match — 94.8% match based on chemical composition and mechanical property overlap.

EN 10088-1 X2CrNiMnMoCuN24-4-3-2 (EN 10088-1:2014) and ASTM A276/A276M S82441 (ASTM A276/A276M:2017) are both steel grades. Both fall under the Stainless Steel category. EN 10088-1 X2CrNiMnMoCuN24-4-3-2 is defined under European Standard (EN), originating from Europe, while ASTM A276/A276M S82441 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-1 X2CrNiMnMoCuN24-4-3-2 vs ASTM A276/A276M S82441 is a 94.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.8%.

Frequently Compared With EN 10088-1 X2CrNiMnMoCuN24-4-3-2:
ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
94.8%
MECHANICAL MATCH
No shared data
OVERALL
94.8%
Specifications
Property EN 10088-1 X2CrNiMnMoCuN24-4-3-2 ASTM A276/A276M S82441
Standard EN 10088-1:2014 ASTM A276/A276M:2017
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=0.70 Not specified
Mn (%) 2.50-4.0 2.5-4.0
P (%) <=0.035 <=0.035
S (%) <=0.005 <=0.005
Cr (%) 23.0-25.0 23.0-25.0
Mo (%) 1.00-2.00 1.00-2.00
Ni (%) 3.0-4.5 3.0-4.5
N (%) 0.20-0.30 0.20-0.30
Cu (%) 0.10-0.80 0.10-0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X2CrNiMnMoCuN24-4-3-2 ASTM A276/A276M S82441
Tensile Strength Not specified >=740 MPa
Yield Strength Not specified >=540 MPa
Elongation Not specified >=25%
Hardness Not specified <=290 HB
Condition Not specified Condition A (Annealed), hot-finished or cold-finished, under 7/16 [11 mm] sizes (first row printed)
Typical Applications
EN 10088-1 X2CrNiMnMoCuN24-4-3-2
Not documented
ASTM A276/A276M S82441
Stainless steel bars and shapes (hot-finished or cold-finished)
Key Differences
Can EN 10088-1 X2CrNiMnMoCuN24-4-3-2 Be Substituted With ASTM A276/A276M S82441?
EN 10088-1 X2CrNiMnMoCuN24-4-3-2 and ASTM A276/A276M S82441 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S82441 is often considered as a substitute for EN 10088-1 X2CrNiMnMoCuN24-4-3-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
EN 10088-1 X2CrNiMnMoCuN24-4-3-2
0 active listings and RFQs →
ASTM A276/A276M S82441
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X2CrNiMnMoCuN24-4-3-2 and ASTM A276/A276M S82441?
EN 10088-1 X2CrNiMnMoCuN24-4-3-2 specifies Si which is not specified for ASTM A276/A276M S82441.
Can EN 10088-1 X2CrNiMnMoCuN24-4-3-2 be substituted with ASTM A276/A276M S82441?
EN 10088-1 X2CrNiMnMoCuN24-4-3-2 and ASTM A276/A276M S82441 overlap closely enough on chemistry and mechanical properties that ASTM A276/A276M S82441 is often considered as a substitute for EN 10088-1 X2CrNiMnMoCuN24-4-3-2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.