EN 10088-1 X4CrNiMo16-5 vs DIN EN ISO 4957 1.2379

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-1 X4CrNiMo16-5 (EN 10088-1:2014) and DIN EN ISO 4957 1.2379 (DIN EN ISO 4957:2018-11) are both steel grades. Both fall under the Tool & Die Steels category. EN 10088-1 X4CrNiMo16-5 is typically used for plastic injection moulds, die casting dies for zinc/aluminium, while DIN EN ISO 4957 1.2379 is commonly used for blanking dies, forming dies, thread rolling dies, punches, shear blades, gauges, broaches, drawing dies. EN 10088-1 X4CrNiMo16-5 is defined under European Standard (EN), originating from Europe, while DIN EN ISO 4957 1.2379 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-1 X4CrNiMo16-5 vs DIN EN ISO 4957 1.2379 is a 53.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-1 X4CrNiMo16-5:
EN ISO 4957 1.2316 DIN EN ISO 4957 1.2344 EN ISO 683-17 100Cr6 GB/T 1299 4Cr5MoSiV GOST 5950 4H5MFS1 GB/T 1299 4Cr5MoSiV1 GOST 5950 4H5MFS AISI 52100 GOST 5950 3H2W8F GB/T 1299 3Cr2W8V IS 3748 103T3 IS 1570 (Part 6) 103T3
Match Breakdown
CHEMISTRY MATCH
53.4%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10088-1 X4CrNiMo16-5 DIN EN ISO 4957 1.2379
Standard EN 10088-1:2014 DIN EN ISO 4957:2018-11
Category Tool & Die Steels Tool & Die Steels
C (%) ≤0.06 1.50–1.60
Si (%) ≤0.70 0.10–0.40
Mn (%) ≤1.50 0.25–0.60
Cr (%) 15.0–17.0 11.00–13.00
Mo (%) 0.80–1.50 0.70–1.00
Ni (%) 3.50–5.50 Not specified
V (%) Not specified 0.80–1.10
S (%) Not specified ≤0.030
P (%) Not specified ≤0.030
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-1 X4CrNiMo16-5 DIN EN ISO 4957 1.2379
Hardness HRC 28–34 (delivered) Not specified
Hardness HRC (hardened) 38–42 Not specified
Corrosion Resistance Good Not specified
Hardness (annealed) Not specified ≤255 HB
Hardness (hardened) Not specified 58–62 HRC
Compressive Strength Not specified 2600 MPa
Typical Applications
EN 10088-1 X4CrNiMo16-5
Plastic injection moulds, die casting dies for zinc/aluminium
DIN EN ISO 4957 1.2379
Blanking dies, forming dies, thread rolling dies, punches, shear blades, gauges, broaches, drawing dies
Key Differences
Can EN 10088-1 X4CrNiMo16-5 Be Substituted With DIN EN ISO 4957 1.2379?
EN 10088-1 X4CrNiMo16-5 and DIN EN ISO 4957 1.2379 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-1 X4CrNiMo16-5
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 3700–4000 mm (145.67–157.48 in)
DIN EN ISO 4957 1.2379
Round Bar → (2 listings)
Diameter: 80–80 mm (3.15–3.15 in)
Length: 2800–3300 mm (110.24–129.92 in)
On M-EX Right Now
EN 10088-1 X4CrNiMo16-5
2 active listings and RFQs →
DIN EN ISO 4957 1.2379
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-1 X4CrNiMo16-5 and DIN EN ISO 4957 1.2379?
EN 10088-1 X4CrNiMo16-5 specifies Ni which is not specified for DIN EN ISO 4957 1.2379. DIN EN ISO 4957 1.2379 specifies V, S, P which are not specified for EN 10088-1 X4CrNiMo16-5.
Can EN 10088-1 X4CrNiMo16-5 be substituted with DIN EN ISO 4957 1.2379?
EN 10088-1 X4CrNiMo16-5 and DIN EN ISO 4957 1.2379 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.