EN 10088-2:2014 X1NiCrMoCu31-27-4 Steel: Specifications & Listings
EN 10088-2:2014 X1NiCrMoCu31-27-4: X1NiCrMoCu31-27-4: austenitic corrosion resisting stainless steel, material number 1.4563. Specified in EN 10088-2:2014.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Si
Mn
P
S
Cr
Mo
Ni
N
Cu
<=0.020
<=0.70
<=2.00
<=0.030
<=0.010
26.0-28.0
3.0-4.0
30.0-32.0
<=0.10
0.70-1.50
Mechanical Properties
Tensile Strength
500-700 MPa
Yield Strength
>=220 MPa
Elongation
>=40%
Condition
Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
More data from EN 10088-2:2014
From the standard
Mechanical properties by product form and thickness1 product form
Product form
Max thickness (mm)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
Rm (MPa)
A80 min, under 3 mm thick (%)
A min, 3 mm and over (%)
Hot rolled plate
75
220
260
500 to 700
40
40
Solution annealed condition; proof strength and elongation are minimum transverse values.
Source: EN 10088-2:2014, Table 7
Impact energy KV2 (ISO-V)1 rows
Product form
Max thickness (mm)
KV2 longitudinal, min (J)
KV2 transverse, min (J)
Hot rolled plate
75
100
60
Applies to products more than 10 mm thick, ISO-V notch, room temperature.
Source: EN 10088-2:2014, Table 7
Proof strength at elevated temperature10 temperatures
Temperature (deg C)
Rp0.2 min (MPa)
Rp1.0 min (MPa)
100
190
220
150
175
205
200
160
190
250
155
185
300
150
180
350
145
175
400
135
165
450
125
155
500
120
150
550
115
145
Minimum values, solution annealed (+AT).
Source: EN 10088-2:2014, Table 12
Hot forming and solution annealingguideline temperatures
Hot forming temperature
1150 to 850 deg C
Cooling after hot forming
air
Heat treatment symbol
+AT
Solution annealing temperature
1070 to 1150 deg C
Cooling after solution annealing
water, air
Informative guideline; cooling must be rapid enough to avoid intergranular corrosion.
Source: EN 10088-2:2014, Table A.1