EN 10088-2 X1NiCrMoCu31-27-4 vs IS 6603 X01Ni31Cr27Mo4Cu
Strong Match — 86.7% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X1NiCrMoCu31-27-4 (EN 10088-2:2014) and IS 6603 X01Ni31Cr27Mo4Cu (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X1NiCrMoCu31-27-4 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 6603 X01Ni31Cr27Mo4Cu is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
EN 10088-2 X1NiCrMoCu31-27-4 is defined under European Standard (EN), originating from Europe, while IS 6603 X01Ni31Cr27Mo4Cu is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-2 X1NiCrMoCu31-27-4 vs IS 6603 X01Ni31Cr27Mo4Cu is a 100% match.
As per mechanical properties, the match is 60%.
Combined, this makes them a strong match overall at 86.7%.
Frequently Compared With EN 10088-2 X1NiCrMoCu31-27-4:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X1NiCrMoCu31-27-4
IS 6603 X01Ni31Cr27Mo4Cu
Tensile Strength
500-700 MPa
500-750 MPa
Yield Strength
>=220 MPa
>=220 MPa
Elongation
>=40%
>=35%
Condition
Solution annealed (+AT), hot rolled plate, up to 75 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-2 X1NiCrMoCu31-27-4
General purposes, hot or cold rolled sheet/plate and strip
IS 6603 X01Ni31Cr27Mo4Cu
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-2 X1NiCrMoCu31-27-4 Be Substituted With IS 6603 X01Ni31Cr27Mo4Cu?
EN 10088-2 X1NiCrMoCu31-27-4 and IS 6603 X01Ni31Cr27Mo4Cu overlap closely enough on chemistry and mechanical properties that IS 6603 X01Ni31Cr27Mo4Cu is often considered as a substitute for EN 10088-2 X1NiCrMoCu31-27-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between EN 10088-2 X1NiCrMoCu31-27-4 and IS 6603 X01Ni31Cr27Mo4Cu?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X1NiCrMoCu31-27-4 be substituted with IS 6603 X01Ni31Cr27Mo4Cu?
EN 10088-2 X1NiCrMoCu31-27-4 and IS 6603 X01Ni31Cr27Mo4Cu overlap closely enough on chemistry and mechanical properties that IS 6603 X01Ni31Cr27Mo4Cu is often considered as a substitute for EN 10088-2 X1NiCrMoCu31-27-4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.