Minimal Match — 39.4% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X2CrMnNiTi12 (EN 10088-2:2014) and EN 10088-1 1.4845 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X2CrMnNiTi12 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while EN 10088-1 1.4845 is commonly used for furnace parts, heat exchangers, kiln components.
EN 10088-2 X2CrMnNiTi12 is defined under European Standard (EN), originating from Europe, while EN 10088-1 1.4845 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10088-2 X2CrMnNiTi12 vs EN 10088-1 1.4845 is a 59.1% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 39.4%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X2CrMnNiTi12
EN 10088-1 1.4845
Tensile Strength
500-650 MPa
≥515 MPa
Condition
Annealed (+A), hot rolled strip, up to 10 mm thick; Yield Strength is Rp0.2 (transverse; longitudinal not given); Elongation is A80 (under 3 mm) or A (3 mm and over)
Not specified
Elongation
>=20%
≥40%
Yield Strength
>=375 MPa
≥205 MPa
Max Service Temp
Not specified
1100°C continuous
Typical Applications
EN 10088-2 X2CrMnNiTi12
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 1.4845
Furnace parts, heat exchangers, kiln components
Key Differences
EN 10088-2 X2CrMnNiTi12 specifies P, S, N, Ti which are not specified for EN 10088-1 1.4845.
Can EN 10088-2 X2CrMnNiTi12 Be Substituted With EN 10088-1 1.4845?
EN 10088-2 X2CrMnNiTi12 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X2CrMnNiTi12 and EN 10088-1 1.4845?
EN 10088-2 X2CrMnNiTi12 specifies P, S, N, Ti which are not specified for EN 10088-1 1.4845.
Can EN 10088-2 X2CrMnNiTi12 be substituted with EN 10088-1 1.4845?
EN 10088-2 X2CrMnNiTi12 and EN 10088-1 1.4845 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.