EN 10088-2 X2CrMnNiTi12 vs IS 1570 (Part 7) 12Cr12MoVH

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrMnNiTi12 (EN 10088-2:2014) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrMnNiTi12 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while IS 1570 (Part 7) 12Cr12MoVH is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature. EN 10088-2 X2CrMnNiTi12 is defined under European Standard (EN), originating from Europe, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, EN 10088-2 X2CrMnNiTi12 vs IS 1570 (Part 7) 12Cr12MoVH is a 56.3% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With EN 10088-2 X2CrMnNiTi12:
GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
56.3%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property EN 10088-2 X2CrMnNiTi12 IS 1570 (Part 7) 12Cr12MoVH
Standard EN 10088-2:2014 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.08-0.16
Si (%) <=1.00 <=0.60
Mn (%) 1.00-2.50 0.40-1.00
P (%) <=0.040 <=0.040
S (%) <=0.015 <=0.035
Cr (%) 11.0-13.0 11.5-13.00
Ni (%) 0.30-1.00 <=1.0
N (%) <=0.025 Not specified
Ti (%) <=0.35 Not specified
Mo (%) Not specified 0.40-0.80
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrMnNiTi12 IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength 500-650 MPa 770-930 MPa
Condition Annealed (+A), hot rolled strip, up to 10 mm thick; Yield Strength is Rp0.2 (transverse; longitudinal not given); Elongation is A80 (under 3 mm) or A (3 mm and over) Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Elongation >=20% >=15%
Yield Strength >=375 MPa >=585 MPa (0.2 % proof stress)
Typical Applications
EN 10088-2 X2CrMnNiTi12
General purposes, hot or cold rolled sheet/plate and strip
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can EN 10088-2 X2CrMnNiTi12 Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-2 X2CrMnNiTi12 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X2CrMnNiTi12
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrMnNiTi12 and IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-2 X2CrMnNiTi12 specifies N, Ti which are not specified for IS 1570 (Part 7) 12Cr12MoVH. IS 1570 (Part 7) 12Cr12MoVH specifies Mo, V which are not specified for EN 10088-2 X2CrMnNiTi12.
Can EN 10088-2 X2CrMnNiTi12 be substituted with IS 1570 (Part 7) 12Cr12MoVH?
EN 10088-2 X2CrMnNiTi12 and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.