EN 10088-2 X2CrMnNiTi12 vs GOST 5632 08X18H10

Minimal Match — 39.4% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrMnNiTi12 (EN 10088-2:2014) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrMnNiTi12 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications. EN 10088-2 X2CrMnNiTi12 is defined under European Standard (EN) (Europe).

As per chemical composition, EN 10088-2 X2CrMnNiTi12 vs GOST 5632 08X18H10 is a 59.1% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 39.4%.

Frequently Compared With EN 10088-2 X2CrMnNiTi12:
EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H ASTM A959 .- GOST 5632 06Kh23N28 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401
Match Breakdown
CHEMISTRY MATCH
59.1%
MECHANICAL MATCH
0%
OVERALL
39.4%
Specifications
Property EN 10088-2 X2CrMnNiTi12 GOST 5632 08X18H10
Standard EN 10088-2:2014 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 ≤0.08
Si (%) <=1.00 ≤0.80
Mn (%) 1.00-2.50 ≤2.00
P (%) <=0.040 ≤0.035
S (%) <=0.015 ≤0.020
Cr (%) 11.0-13.0 17.0–19.0
Ni (%) 0.30-1.00 9.0–11.0
N (%) <=0.025 Not specified
Ti (%) <=0.35 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrMnNiTi12 GOST 5632 08X18H10
Tensile Strength 500-650 MPa ≥520 MPa
Condition Annealed (+A), hot rolled strip, up to 10 mm thick; Yield Strength is Rp0.2 (transverse; longitudinal not given); Elongation is A80 (under 3 mm) or A (3 mm and over) Not specified
Elongation >=20% ≥40%
Yield Strength >=375 MPa ≥205 MPa
Typical Applications
EN 10088-2 X2CrMnNiTi12
General purposes, hot or cold rolled sheet/plate and strip
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can EN 10088-2 X2CrMnNiTi12 Be Substituted With GOST 5632 08X18H10?
EN 10088-2 X2CrMnNiTi12 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
EN 10088-2 X2CrMnNiTi12
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
EN 10088-2 X2CrMnNiTi12
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrMnNiTi12 and GOST 5632 08X18H10?
EN 10088-2 X2CrMnNiTi12 specifies N, Ti which are not specified for GOST 5632 08X18H10.
Can EN 10088-2 X2CrMnNiTi12 be substituted with GOST 5632 08X18H10?
EN 10088-2 X2CrMnNiTi12 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.