EN 10088-2 X2CrNiMnMoN25-18-6-5 vs ASTM A959 317LM

Related Material — 68.5% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrNiMnMoN25-18-6-5 (EN 10088-2:2014) and ASTM A959 317LM (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrNiMnMoN25-18-6-5 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A959 317LM is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-2 X2CrNiMnMoN25-18-6-5 is defined under European Standard (EN), originating from Europe, while ASTM A959 317LM is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-2 X2CrNiMnMoN25-18-6-5 vs ASTM A959 317LM is a 68.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 68.5%.

Frequently Compared With EN 10088-2 X2CrNiMnMoN25-18-6-5:
IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H EN 10088-1 1.4301 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
68.5%
MECHANICAL MATCH
No shared data
OVERALL
68.5%
Specifications
Property EN 10088-2 X2CrNiMnMoN25-18-6-5 ASTM A959 317LM
Standard EN 10088-2:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) 5.0-7.0 <=2.00
P (%) <=0.030 <=0.045
S (%) <=0.015 <=0.030
Cr (%) 24.0-26.0 18.0-20.0
Mo (%) 4.0-5.0 4.0-5.0
Ni (%) 16.0-19.0 13.5-17.5
N (%) 0.30-0.60 <=0.20
Nb (%) <=0.15 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrNiMnMoN25-18-6-5 ASTM A959 317LM
Tensile Strength 800-950 MPa Not specified
Yield Strength >=420 MPa Not specified
Elongation >=30% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 6 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X2CrNiMnMoN25-18-6-5
General purposes, hot or cold rolled sheet/plate and strip
ASTM A959 317LM
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can EN 10088-2 X2CrNiMnMoN25-18-6-5 Be Substituted With ASTM A959 317LM?
EN 10088-2 X2CrNiMnMoN25-18-6-5 and ASTM A959 317LM share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X2CrNiMnMoN25-18-6-5
0 active listings and RFQs →
ASTM A959 317LM
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrNiMnMoN25-18-6-5 and ASTM A959 317LM?
EN 10088-2 X2CrNiMnMoN25-18-6-5 specifies Nb which is not specified for ASTM A959 317LM.
Can EN 10088-2 X2CrNiMnMoN25-18-6-5 be substituted with ASTM A959 317LM?
EN 10088-2 X2CrNiMnMoN25-18-6-5 and ASTM A959 317LM share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.