Close Alternative — 81.9% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X2CrTi17 (EN 10088-2:2014) and EN 10088-1 X2CrNbZr17 (EN 10088-1:2023) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X2CrTi17 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X2CrNbZr17 is defined under European Standard (EN), originating from Europe.
As per chemical composition, EN 10088-2 X2CrTi17 vs EN 10088-1 X2CrNbZr17 is a 81.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 81.9%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X2CrTi17
EN 10088-1 X2CrNbZr17
Tensile Strength
380-530 MPa
Not specified
Condition
Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Not specified
Yield Strength
>=180 MPa
Not specified
Elongation
>=24%
Not specified
Typical Applications
EN 10088-2 X2CrTi17
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X2CrNbZr17
Not documented
Key Differences
EN 10088-2 X2CrTi17 specifies N, Ti which are not specified for EN 10088-1 X2CrNbZr17.
Can EN 10088-2 X2CrTi17 Be Substituted With EN 10088-1 X2CrNbZr17?
EN 10088-2 X2CrTi17 and EN 10088-1 X2CrNbZr17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between EN 10088-2 X2CrTi17 and EN 10088-1 X2CrNbZr17?
EN 10088-2 X2CrTi17 specifies N, Ti which are not specified for EN 10088-1 X2CrNbZr17.
Can EN 10088-2 X2CrTi17 be substituted with EN 10088-1 X2CrNbZr17?
EN 10088-2 X2CrTi17 and EN 10088-1 X2CrNbZr17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.