EN 10088-2:2014 X2CrTi24 Steel: Specifications & Listings

EN 10088-2:2014 X2CrTi24: X2CrTi24: ferritic corrosion resisting stainless steel, material number 1.4613. Specified in EN 10088-2:2014.

Category: Stainless Steel
Grade Details
GradeEN 10088-2:2014 X2CrTi24
Standard EN 10088-2:2014
ApplicationsGeneral purposes, hot or cold rolled sheet/plate and strip
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
EN 10088-1 X2CrTi21 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-1 X2CrTi24 EN 10088-1:2014 Europe (CEN) No activity yet
EN 10088-3 X2CrTi24 EN 10088-3:2014 Europe No activity yet
EN 10088-2 X2CrTi21 EN 10088-2:2014 Europe No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X2CrTi24 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrTi24 EN 10088-1:2023 Strong Match
EN 10088-2 X2CrTi21 EN 10088-2:2014 Strong Match
EN 10088-3 X2CrTi24 EN 10088-3:2014 Strong Match
EN 10088-1 X2CrTi21 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrTi21 EN 10088-1:2023 Strong Match
EN 10088-3 X2CrTi21 EN 10088-3:2014 Close Alternative
ASTM A959 2304 ASTM A959:2011 Related Material
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Mo Ni Ti Cu Al
<=0.030 <=1.00 <=1.00 <=0.050 <=0.050 22.0-25.0 <=0.50 <=0.50 <=1.00 <=0.50 <=0.05
Mechanical Properties
Tensile Strength 430-630 MPa
Condition Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Yield Strength >=230 MPa
Elongation >=18%

More data from EN 10088-2:2014

From the standard
Mechanical properties by product form and thickness 1 product form
Product formMax thickness (mm)Rp0.2 longitudinal, min (MPa)Rp0.2 transverse, min (MPa)Rm (MPa)A80 min, under 3 mm thick (%)A min, 3 mm and over (%)
Cold rolled strip8230250430 to 6301818
Annealed condition; one elongation value is printed for both thickness classes.
Source: EN 10088-2:2014, Table 9
Proof strength at elevated temperature 7 temperatures
Temperature (deg C)Rp0.2 min (MPa)
100230
150220
200210
250205
300200
350180
400-
Minimum values, annealed (+A).
Source: EN 10088-2:2014, Table 14
Hot forming and annealing guideline temperatures
Hot forming temperature
1100 to 800 deg C
Cooling after hot forming
air
Heat treatment symbol
+A
Annealing temperature
870 to 930 deg C
Cooling after annealing
air, water
Informative guideline.
Source: EN 10088-2:2014, Table A.3

Active EN 10088-2:2014 X2CrTi24 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-2:2014 X2CrTi24 listings at this time.

Register for Alerts

Buyer RFQs for EN 10088-2:2014 X2CrTi24

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-2:2014 X2CrTi24 at this time.

Register for Alerts