EN 10088-2 X2CrTi24 vs ASTM A959 2304

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

EN 10088-2 X2CrTi24 (EN 10088-2:2014) and ASTM A959 2304 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X2CrTi24 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while ASTM A959 2304 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). EN 10088-2 X2CrTi24 is defined under European Standard (EN), originating from Europe, while ASTM A959 2304 is defined under ASTM International, originating from United States.

As per chemical composition, EN 10088-2 X2CrTi24 vs ASTM A959 2304 is a 70.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With EN 10088-2 X2CrTi24:
ASTM A959 .- GOST 5632 06Kh23N28 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
70.7%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property EN 10088-2 X2CrTi24 ASTM A959 2304
Standard EN 10088-2:2014 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
Mn (%) <=1.00 <=2.50
P (%) <=0.050 <=0.040
S (%) <=0.050 <=0.030
Cr (%) 22.0-25.0 21.5-24.5
Mo (%) <=0.50 0.05-0.60
Ni (%) <=0.50 3.0-5.5
Ti (%) <=1.00 Not specified
Cu (%) <=0.50 0.05-0.60
Al (%) <=0.05 Not specified
N (%) Not specified 0.05-0.20
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X2CrTi24 ASTM A959 2304
Tensile Strength 430-630 MPa Not specified
Condition Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse Not specified
Yield Strength >=230 MPa Not specified
Elongation >=18% Not specified
Typical Applications
EN 10088-2 X2CrTi24
General purposes, hot or cold rolled sheet/plate and strip
ASTM A959 2304
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can EN 10088-2 X2CrTi24 Be Substituted With ASTM A959 2304?
EN 10088-2 X2CrTi24 and ASTM A959 2304 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
EN 10088-2 X2CrTi24
0 active listings and RFQs →
ASTM A959 2304
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X2CrTi24 and ASTM A959 2304?
EN 10088-2 X2CrTi24 specifies Ti, Al which are not specified for ASTM A959 2304. ASTM A959 2304 specifies N which is not specified for EN 10088-2 X2CrTi24.
Can EN 10088-2 X2CrTi24 be substituted with ASTM A959 2304?
EN 10088-2 X2CrTi24 and ASTM A959 2304 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.