Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
EN 10088-2 X2CrTi24 (EN 10088-2:2014) and GOST 5632 06Kh23N28 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-2 X2CrTi24 is typically used for general purposes, hot or cold rolled sheet/plate and strip, while GOST 5632 06Kh23N28 is commonly used for furnace components, heat exchangers, high temperature applications.
EN 10088-2 X2CrTi24 is defined under European Standard (EN) (Europe).
As per chemical composition, EN 10088-2 X2CrTi24 vs GOST 5632 06Kh23N28 is a 62.5% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-2 X2CrTi24
GOST 5632 06Kh23N28
Tensile Strength
430-630 MPa
≥510 MPa
Condition
Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Not specified
Yield Strength
>=230 MPa
≥196 MPa
Elongation
>=18%
≥35%
Max Service Temp
Not specified
1050°C
Typical Applications
EN 10088-2 X2CrTi24
General purposes, hot or cold rolled sheet/plate and strip
GOST 5632 06Kh23N28
Furnace components, heat exchangers, high temperature applications
Key Differences
EN 10088-2 X2CrTi24 specifies P, S, Mo, Ti which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-2 X2CrTi24 Be Substituted With GOST 5632 06Kh23N28?
EN 10088-2 X2CrTi24 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-2 X2CrTi24 and GOST 5632 06Kh23N28?
EN 10088-2 X2CrTi24 specifies P, S, Mo, Ti which are not specified for GOST 5632 06Kh23N28.
Can EN 10088-2 X2CrTi24 be substituted with GOST 5632 06Kh23N28?
EN 10088-2 X2CrTi24 and GOST 5632 06Kh23N28 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.