EN 10088-2:2014 X6Cr13 Steel: Specifications & Listings

EN 10088-2:2014 X6Cr13: X6Cr13: ferritic corrosion resisting stainless steel, material number 1.4000. Specified in EN 10088-2:2014.

Category: Stainless Steel
Grade Details
GradeEN 10088-2:2014 X6Cr13
Standard EN 10088-2:2014
ApplicationsGeneral purposes, hot or cold rolled sheet/plate and strip
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 S41603 ASTM A959:2011 USA No activity yet
ASTM A959 410S ASTM A959:2011 USA No activity yet
ASTM A959 416 ASTM A959:2011 USA No activity yet
ASTM A959 416Se ASTM A959:2011 USA No activity yet
EN 10088-1 X6Cr13 EN 10088-1:2014 Europe (CEN) No activity yet
ASTM A959 SS410 ASTM A959:2011 USA 3 listings, 0 RFQs →
ASTM A959 410Cb ASTM A959:2011 USA No activity yet
ASTM A959 429 ASTM A959:2011 USA No activity yet
ASTM A959 403 ASTM A959:2011 USA No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X6Cr13 EN 10088-1:2014 Strong Match
EN 10088-1 X6Cr13 EN 10088-1:2023 Strong Match
EN 10088-1 X6CrAl13 EN 10088-1:2014 Strong Match
EN 10088-1 X6CrAl13 EN 10088-1:2023 Strong Match
ASTM A959 410S ASTM A959:2011 Strong Match
ASTM A959 S41603 ASTM A959:2011 Strong Match
ASTM A959 416Se ASTM A959:2011 Strong Match
EN 10088-1 X15Cr13 EN 10088-1:2014 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr
<=0.08 <=1.00 <=1.00 <=0.040 <=0.015 12.0-14.0
Mechanical Properties
Tensile Strength 400-600 MPa
Condition Annealed (+A), cold rolled strip, up to 8 mm thick; Elongation is A80 (under 3 mm) or A (3 mm and over), longitudinal and transverse
Yield Strength >=240 MPa
Elongation >=19%

More data from EN 10088-2:2014

From the standard
Mechanical properties by product form and thickness 3 product forms
Product formMax thickness (mm)Rp0.2 longitudinal, min (MPa)Rp0.2 transverse, min (MPa)Rm (MPa)A80 min, under 3 mm thick (%)A min, 3 mm and over (%)
Cold rolled strip8240250400 to 6001919
Hot rolled strip13.5220230400 to 6001919
Hot rolled plate25220230400 to 6001919
Annealed condition; one elongation value is printed for both thickness classes.
Source: EN 10088-2:2014, Table 9
Proof strength at elevated temperature 7 temperatures
Temperature (deg C)Rp0.2 min (MPa)
100220
150215
200210
250205
300200
350195
400190
Minimum values, annealed (+A).
Source: EN 10088-2:2014, Table 14
Hot forming and annealing guideline temperatures
Hot forming temperature
1100 to 800 deg C
Cooling after hot forming
air
Heat treatment symbol
+A
Annealing temperature
750 to 810 deg C
Cooling after annealing
air, water
Informative guideline.
Source: EN 10088-2:2014, Table A.3

Active EN 10088-2:2014 X6Cr13 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-2:2014 X6Cr13 listings at this time.

Register for Alerts

Buyer RFQs for EN 10088-2:2014 X6Cr13

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-2:2014 X6Cr13 at this time.

Register for Alerts