EN 10088-2 X8CrMnNi19-6-3 vs EN 10088-1 X12CrMnNiN17-7-5

Close Alternative — 81.1% match based on chemical composition and mechanical property overlap.

EN 10088-2 X8CrMnNi19-6-3 (EN 10088-2:2014) and EN 10088-1 X12CrMnNiN17-7-5 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. EN 10088-2 X8CrMnNi19-6-3 is defined under European Standard (EN), originating from Europe, while EN 10088-1 X12CrMnNiN17-7-5 is defined under European Standard (EN), originating from Europe.

As per chemical composition, EN 10088-2 X8CrMnNi19-6-3 vs EN 10088-1 X12CrMnNiN17-7-5 is a 81.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 81.1%.

Frequently Compared With EN 10088-2 X8CrMnNi19-6-3:
ASTM A959 .- GOST 5632 08X18H10 ASTM A959 201 ASTM A959 202 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
81.1%
MECHANICAL MATCH
No shared data
OVERALL
81.1%
Specifications
Property EN 10088-2 X8CrMnNi19-6-3 EN 10088-1 X12CrMnNiN17-7-5
Standard EN 10088-2:2014 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.10 <=0.15
Si (%) <=1.00 <=1.00
Mn (%) 5.0-8.0 5.5-7.5
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Cr (%) 17.0-20.5 16.0-18.0
Ni (%) 2.00-4.5 3.5-5.5
N (%) <=0.30 0.05-0.25
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property EN 10088-2 X8CrMnNi19-6-3 EN 10088-1 X12CrMnNiN17-7-5
Tensile Strength 600-900 MPa Not specified
Yield Strength >=400 MPa Not specified
Elongation >=40% Not specified
Condition Solution annealed (+AT), cold rolled strip, up to 4 mm thick; Yield Strength is Rp0.2 (transverse), Elongation is A80 for under 3 mm thick Not specified
Typical Applications
EN 10088-2 X8CrMnNi19-6-3
General purposes, hot or cold rolled sheet/plate and strip
EN 10088-1 X12CrMnNiN17-7-5
Not documented
Can EN 10088-2 X8CrMnNi19-6-3 Be Substituted With EN 10088-1 X12CrMnNiN17-7-5?
EN 10088-2 X8CrMnNi19-6-3 and EN 10088-1 X12CrMnNiN17-7-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
EN 10088-2 X8CrMnNi19-6-3
0 active listings and RFQs →
EN 10088-1 X12CrMnNiN17-7-5
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between EN 10088-2 X8CrMnNi19-6-3 and EN 10088-1 X12CrMnNiN17-7-5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-2 X8CrMnNi19-6-3 be substituted with EN 10088-1 X12CrMnNiN17-7-5?
EN 10088-2 X8CrMnNi19-6-3 and EN 10088-1 X12CrMnNiN17-7-5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.