EN 10088-3:2014 X15Cr13 Steel: Specifications, Equivalents & Listings

Category: Stainless Steel

Grade Details

Grade	EN 10088-3:2014 X15Cr13
Standard	EN 10088-3:2014
Applications	General purposes, semi-finished products, bars, rods, wire, sections and bright products

Equivalent / Similar Grades

Grade	Standard	Region	Live on M-EX
ASTM A959 416Se	ASTM A959:2011	USA	No activity yet
ASTM A959 420	ASTM A959:2011	USA	No activity yet
EN 10088-1 X15Cr13	EN 10088-1:2014	Europe (CEN)	No activity yet
ASTM A959 SS410	ASTM A959:2011	USA	3 listings, 0 RFQs →
ASTM A959 410Cb	ASTM A959:2011	USA	No activity yet
ASTM A959 410S	ASTM A959:2011	USA	No activity yet
ASTM A959 416	ASTM A959:2011	USA	No activity yet
ASTM A959 S41603	ASTM A959:2011	USA	No activity yet
ASTM A959 403	ASTM A959:2011	USA	No activity yet

Grade ComparisonCompare With a Specific Grade →

Grade	Standard	Match
EN 10088-1 X15Cr13	EN 10088-1:2014	Strong Match
EN 10088-1 X15Cr13	EN 10088-1:2023	Strong Match
ASTM A959 420	ASTM A959:2011	Strong Match
EN 10088-1 X6Cr13	EN 10088-1:2014	Strong Match
EN 10088-1 X6Cr13	EN 10088-1:2023	Strong Match
ASTM A959 SS410	ASTM A959:2011	Strong Match
ASTM A959 416Se	ASTM A959:2011	Strong Match
EN 10088-1 X20Cr13	EN 10088-1:2014	Strong Match

Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.

Chemical Composition (%)

C	Si	Mn	P	S	Cr
0.12-0.17	<=1.00	<=1.00	<=0.040	<=0.030	12.0-14.0

Mechanical Properties

Tensile Strength	<=730 MPa
Hardness	<=220 HB
Condition	Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, size range not stated; hardness for guidance only

More data from EN 10088-3:2014

From the standard

Mechanical properties by heat treatment condition 2 rows

Thickness or diameter (mm)	Condition	Hardness HBW, max (guidance)	Rp0.2 min (MPa)	Rm (MPa)	A min, longitudinal (%)	A min, transverse (%)	KV2 min, longitudinal (J)	KV2 min, transverse (J)
-	+A	220	-	max. 730	-	-	-	-
up to 160	+QT650	-	450	650 to 850	15	-	-	-

+A = annealed, +QT = quenched and tempered; for rods only the tensile strength values apply.

Source: EN 10088-3:2014, Table 11

Proof strength at elevated temperature 7 temperatures

Temperature (deg C)	Rp0.2 min, +QT650 (MPa)
100	420
150	410
200	400
250	385
300	365
350	-
400	300

Minimum values.

Source: EN 10088-3:2014, Table 23

Hot forming and heat treatment 2 conditions

Condition	Annealing temperature (deg C)	Cooling after annealing	Quenching temperature (deg C)	Quenching medium	Tempering temperature (deg C)
+A	750 to 800	furn., air	-	-	-
+QT650	-	-	950 to 1030	oil, air	700 to 750

Hot forming 1100 to 800 deg C, cooling: slow cooling. Informative guideline.

Source: EN 10088-3:2014, Table A.4

Active EN 10088-3:2014 X15Cr13 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-3:2014 X15Cr13 listings at this time.

Buyer RFQs for EN 10088-3:2014 X15Cr13

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-3:2014 X15Cr13 at this time.

EN 10088-3:2014 X15Cr13 Steel: Specifications & Listings

More data from EN 10088-3:2014

Active EN 10088-3:2014 X15Cr13 Listings on M-EX (For Sale)

Buyer RFQs for EN 10088-3:2014 X15Cr13