EN 10088-3 X1NiCrMoCu31-27-4 vs IS 6603 X01Ni25Cr20Mo5Cu
Related Material — 69.9% match
based on chemical composition and mechanical property overlap.
EN 10088-3 X1NiCrMoCu31-27-4 (EN 10088-3:2014) and IS 6603 X01Ni25Cr20Mo5Cu (IS 6603:2024) are both steel grades.
Both fall under the Stainless Steel category.
EN 10088-3 X1NiCrMoCu31-27-4 is typically used for general purposes, semi-finished products, bars, rods, wire, sections and bright products, while IS 6603 X01Ni25Cr20Mo5Cu is commonly used for general purposes, semi-finished products, bars, wire rods and bright bars.
EN 10088-3 X1NiCrMoCu31-27-4 is defined under European Standard (EN), originating from Europe, while IS 6603 X01Ni25Cr20Mo5Cu is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, EN 10088-3 X1NiCrMoCu31-27-4 vs IS 6603 X01Ni25Cr20Mo5Cu is a 69.3% match.
As per mechanical properties, the match is 93.3%.
Combined, this makes them a related material overall at 69.9%.
Frequently Compared With EN 10088-3 X1NiCrMoCu31-27-4:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
EN 10088-3 X1NiCrMoCu31-27-4
IS 6603 X01Ni25Cr20Mo5Cu
Tensile Strength
500-750 MPa
530-730 MPa
Yield Strength
>=220 MPa
>=220 MPa
Elongation
>=35%
>=35%
Hardness
<=230 HB
Not specified
Condition
Solution annealed (+AT), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only
Solution annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 160 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal)
Typical Applications
EN 10088-3 X1NiCrMoCu31-27-4
General purposes, semi-finished products, bars, rods, wire, sections and bright products
IS 6603 X01Ni25Cr20Mo5Cu
General purposes, semi-finished products, bars, wire rods and bright bars
Can EN 10088-3 X1NiCrMoCu31-27-4 Be Substituted With IS 6603 X01Ni25Cr20Mo5Cu?
EN 10088-3 X1NiCrMoCu31-27-4 and IS 6603 X01Ni25Cr20Mo5Cu share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between EN 10088-3 X1NiCrMoCu31-27-4 and IS 6603 X01Ni25Cr20Mo5Cu?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can EN 10088-3 X1NiCrMoCu31-27-4 be substituted with IS 6603 X01Ni25Cr20Mo5Cu?
EN 10088-3 X1NiCrMoCu31-27-4 and IS 6603 X01Ni25Cr20Mo5Cu share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.