EN 10088-3:2014 X6Cr13 Steel: Specifications & Listings

EN 10088-3:2014 X6Cr13: X6Cr13: ferritic corrosion resisting stainless steel, material number 1.4000. Specified in EN 10088-3:2014.

Category: Stainless Steel
Grade Details
GradeEN 10088-3:2014 X6Cr13
Standard EN 10088-3:2014
ApplicationsGeneral purposes, semi-finished products, bars, rods, wire, sections and bright products
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ASTM A959 S41603 ASTM A959:2011 USA No activity yet
ASTM A959 429 ASTM A959:2011 USA No activity yet
ASTM A959 403 ASTM A959:2011 USA No activity yet
ASTM A959 410S ASTM A959:2011 USA No activity yet
ASTM A959 410Cb ASTM A959:2011 USA No activity yet
ASTM A959 416 ASTM A959:2011 USA No activity yet
ASTM A959 416Se ASTM A959:2011 USA No activity yet
EN 10088-1 X6Cr13 EN 10088-1:2014 Europe (CEN) No activity yet
ASTM A959 SS410 ASTM A959:2011 USA 3 listings, 0 RFQs →
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X6Cr13 EN 10088-1:2014 Strong Match
EN 10088-1 X6Cr13 EN 10088-1:2023 Strong Match
ASTM A959 410S ASTM A959:2011 Strong Match
EN 10088-1 X6CrAl13 EN 10088-1:2014 Strong Match
EN 10088-1 X6CrAl13 EN 10088-1:2023 Strong Match
ASTM A959 S41603 ASTM A959:2011 Strong Match
ASTM A959 SS410 ASTM A959:2011 Strong Match
ASTM A959 416Se ASTM A959:2011 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr
<=0.08 <=1.00 <=1.00 <=0.040 <=0.030 12.0-14.0
Mechanical Properties
Tensile Strength 400-630 MPa
Yield Strength >=230 MPa
Elongation >=20%
Hardness <=200 HB
Condition Annealed (+A), conditions 1C, 1E, 1D, 1X, 1G and 2D, thickness or diameter up to 25 mm; Yield Strength is Rp0.2, Elongation is A (longitudinal), hardness for guidance only

More data from EN 10088-3:2014

From the standard
Mechanical properties by thickness or diameter 1 size range
Thickness or diameter, max (mm)Hardness HBW, max (guidance)Rp0.2 min (MPa)Rm (MPa)A min, longitudinal (%)
up to 25200230400 to 63020
Annealed, conditions 1C, 1E, 1D, 1X, 1G and 2D; for rods only the tensile strength values apply.
Source: EN 10088-3:2014, Table 10
Proof strength at elevated temperature 7 temperatures
Temperature (deg C)Rp0.2 min (MPa)
100220
150215
200210
250205
300200
350195
400190
Minimum values, annealed (+A).
Source: EN 10088-3:2014, Table 22
Hot forming and annealing guideline temperatures
Hot forming temperature
1100 to 800 deg C
Cooling after hot forming
air
Heat treatment symbol
+A
Annealing temperature
750 to 800 deg C
Cooling after annealing
air
Informative guideline.
Source: EN 10088-3:2014, Table A.3

Active EN 10088-3:2014 X6Cr13 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active EN 10088-3:2014 X6Cr13 listings at this time.

Register for Alerts

Buyer RFQs for EN 10088-3:2014 X6Cr13

+ Post an RFQ for this grade

No open buyer requirements for EN 10088-3:2014 X6Cr13 at this time.

Register for Alerts