Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
GOST 801 ShKh15 (GOST 801-1978) and IS 1570 (Part 7) 10Cr36Mo10H (IS 1570 (Part 7):1992) are both steel grades.
Both fall under the Alloy Steel category.
GOST 801 ShKh15 is typically used for used for ball bearings, roller bearings, races, bearing rings, and precision rollers., while IS 1570 (Part 7) 10Cr36Mo10H is commonly used for boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature.
IS 1570 (Part 7) 10Cr36Mo10H is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, GOST 801 ShKh15 vs IS 1570 (Part 7) 10Cr36Mo10H is a 64.8% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
GOST 801 ShKh15
IS 1570 (Part 7) 10Cr36Mo10H
Tensile Strength
750-950 MPa
410-560 MPa
Yield Strength
450 MPa min
>=135 MPa (0.2 % proof stress)
Elongation
8% min
>=20%
Hardness
60-66 HRC
Not specified
Condition
Not specified
Pipes, A, thickness - (first row of Table 3)
Typical Applications
GOST 801 ShKh15
Used for ball bearings, roller bearings, races, bearing rings, and precision rollers.
IS 1570 (Part 7) 10Cr36Mo10H
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
IS 1570 (Part 7) 10Cr36Mo10H specifies P, S, Mo, Al (metallic) which are not specified for GOST 801 ShKh15.
Can GOST 801 ShKh15 Be Substituted With IS 1570 (Part 7) 10Cr36Mo10H?
GOST 801 ShKh15 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between GOST 801 ShKh15 and IS 1570 (Part 7) 10Cr36Mo10H?
IS 1570 (Part 7) 10Cr36Mo10H specifies P, S, Mo, Al (metallic) which are not specified for GOST 801 ShKh15.
Can GOST 801 ShKh15 be substituted with IS 1570 (Part 7) 10Cr36Mo10H?
GOST 801 ShKh15 and IS 1570 (Part 7) 10Cr36Mo10H share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.