GOST 801 ShKh15 vs SAE J404 E52100

Strong Match — 87.2% match based on chemical composition and mechanical property overlap.

GOST 801 ShKh15 (GOST 801-1978) and SAE J404 E52100 (SAE J404:2009) are both steel grades. Both fall under the Alloy Steel category. GOST 801 ShKh15 is typically used for used for ball bearings, roller bearings, races, bearing rings, and precision rollers., while SAE J404 E52100 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. SAE J404 E52100 is defined under SAE International (United States).

As per chemical composition, GOST 801 ShKh15 vs SAE J404 E52100 is a 87.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 87.2%.

Frequently Compared With GOST 801 ShKh15:
UNI 11234 100Cr6 NF A35-565 100C6 GOST 4543 12HN3A IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 GB/T 3077 12Cr2Ni4A IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
87.2%
MECHANICAL MATCH
No shared data
OVERALL
87.2%
Specifications
Property GOST 801 ShKh15 SAE J404 E52100
Standard GOST 801-1978 SAE J404:2009
Category Alloy Steel Alloy Steel
C (%) 0.95-1.05 0.98-1.10
Cr (%) 1.35-1.65 1.30-1.60
Mn (%) 0.2-0.5 0.25-0.45
Si (%) 0.17-0.37 0.15-0.35
P (%) Not specified <=0.025
S (%) Not specified <=0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property GOST 801 ShKh15 SAE J404 E52100
Tensile Strength 750-950 MPa Not specified
Yield Strength 450 MPa min Not specified
Elongation 8% min Not specified
Hardness 60-66 HRC Not specified
Typical Applications
GOST 801 ShKh15
Used for ball bearings, roller bearings, races, bearing rings, and precision rollers.
SAE J404 E52100
Chemistry-only alloy steel grade; see the composition notes for product scope
Key Differences
Can GOST 801 ShKh15 Be Substituted With SAE J404 E52100?
GOST 801 ShKh15 and SAE J404 E52100 overlap closely enough on chemistry and mechanical properties that SAE J404 E52100 is often considered as a substitute for GOST 801 ShKh15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
GOST 801 ShKh15
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6600–7000 mm (259.84–275.59 in)
SAE J404 E52100
No active listings currently.
On M-EX Right Now
GOST 801 ShKh15
2 active listings and RFQs →
SAE J404 E52100
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between GOST 801 ShKh15 and SAE J404 E52100?
SAE J404 E52100 specifies P, S which are not specified for GOST 801 ShKh15.
Can GOST 801 ShKh15 be substituted with SAE J404 E52100?
GOST 801 ShKh15 and SAE J404 E52100 overlap closely enough on chemistry and mechanical properties that SAE J404 E52100 is often considered as a substitute for GOST 801 ShKh15 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.