IS 11169 (Part 2) X02Cr17Ni12Mo2 vs ASTM A959 316LN

Strong Match — 92.4% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr17Ni12Mo2 (IS 11169 (Part 2):1989) and ASTM A959 316LN (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr17Ni12Mo2 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while ASTM A959 316LN is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X02Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 316LN is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X02Cr17Ni12Mo2 vs ASTM A959 316LN is a 92.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.4%.

Frequently Compared With IS 11169 (Part 2) X02Cr17Ni12Mo2:
ASTM A959 29-4C GB/T 3280 06Cr19Ni10 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH ASTM A959 .- GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
92.4%
MECHANICAL MATCH
No shared data
OVERALL
92.4%
Specifications
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 ASTM A959 316LN
Standard IS 11169 (Part 2):1989 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Si (%) <=1.0 <=1.00
Mn (%) <=2.0 <=2.00
Ni (%) 10.0-14.0 10.0-13.0
Cr (%) 16.0-18.0 16.0-18.0
Mo (%) 2.0-3.0 2.00-3.00
S (%) <=0.030 <=0.030
P (%) <=0.045 <=0.045
N (%) Not specified 0.10-0.16
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 ASTM A959 316LN
Yield Strength (0.2% proof) >=225 MPa Not specified
Tensile Strength 500-750 MPa Not specified
Elongation >=40% Not specified
Impact (U-notch 5 mm) >=60 J Not specified
Condition Quenched reference test piece (Table 6 treatment) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr17Ni12Mo2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
ASTM A959 316LN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 Be Substituted With ASTM A959 316LN?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and ASTM A959 316LN overlap closely enough on chemistry and mechanical properties that ASTM A959 316LN is often considered as a substitute for IS 11169 (Part 2) X02Cr17Ni12Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr17Ni12Mo2
0 active listings and RFQs →
ASTM A959 316LN
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr17Ni12Mo2 and ASTM A959 316LN?
ASTM A959 316LN specifies N which is not specified for IS 11169 (Part 2) X02Cr17Ni12Mo2.
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 be substituted with ASTM A959 316LN?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and ASTM A959 316LN overlap closely enough on chemistry and mechanical properties that ASTM A959 316LN is often considered as a substitute for IS 11169 (Part 2) X02Cr17Ni12Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.