IS 11169 (Part 2):2023 X02Cr18Ni9Cu3 Steel: Specifications & Listings

IS 11169 (Part 2):2023 X02Cr18Ni9Cu3: Cold heading quality austenitic stainless steel X02Cr18Ni9Cu3 to IS 11169 (Part 2):2023, supplied as wire rod, bars or wire of 0.8 to 50 mm. Maximum tensile strength solution annealed is 590 MPa.

Category: Stainless Steel
Grade Details
GradeIS 11169 (Part 2):2023 X02Cr18Ni9Cu3
Standard IS 11169 (Part 2):2023
ApplicationsCold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
ISO 4567-304-30-I ISO 4954 International Not yet on M-EX
EN X3CrNiCu18-9-4 (1.4567) EN 10263 Europe Not yet on M-EX
JIS SUSXM7 JIS Japan Not yet on M-EX
GB/ISC S30488 GB China Not yet on M-EX
ASTM A959 S30430 ASTM A959:2011 USA No activity yet
EN 10088-1 X3CrNiCu18-9-4 EN 10088-1:2014 Europe (CEN) No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
EN 10088-1 X3CrNiCu18-9-4 EN 10088-1:2014 Strong Match
EN 10088-1 X3CrNiCu18-9-4 EN 10088-1:2023 Strong Match
ASTM A959 S30430 ASTM A959:2011 Strong Match
EN 10088-1 X2CrNi18-9 EN 10088-1:2014 Strong Match
EN 10088-1 X2CrNi18-9 EN 10088-1:2023 Strong Match
BS 970 (Part 3) 304S11 BS 970 (Part 3):1991 Strong Match
BS 970 (Part 1) 304S11 BS 970 (Part 1):1983 Strong Match
ASTM A959 304L ASTM A959:2011 Close Alternative
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Cr Cu Mn N Ni P S Si
<=0.04 17.0-19.0 3.00-4.00 <=2.00 <=0.10 8.5-10.5 <=0.045 <=0.030 <=1.00
Mechanical Properties
Reduction of Area, solution annealed (+AT) >=68% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) <=590 MPa (over 5 to 50 mm)

More data from IS 11169 (Part 2):2023

From the standard
Other composition limits from the table notes
Values
Maximum unless a range is given (ladle analysis)
Steel type
Austenitic
Nickel
A minimum of 8.0 percent is permitted, unless otherwise agreed when ordering
Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.
Source: IS 11169 (Part 2):2023, Table 10 and its notes
Tensile strength and reduction of area by delivery condition by delivery condition and size
Delivery conditionDiameter (mm)Tensile strength, max (MPa)Reduction of area, min (%)
+AT or +AT+PEover 5 to 1059068
+AT or +AT+PEover 10 to 2559068
+AT or +AT+PEover 25 to 5059068
+AT+Cover 5 to 10740-
+AT+Cover 10 to 25700-
+AT+C+AT0.8 to 263068
+AT+C+ATover 2 to 560068
+AT+C+ATover 5 to 1059068
+AT+C+ATover 10 to 2559068
+AT+C+AT+LC0.8 to 268063
+AT+C+AT+LCover 2 to 565063
+AT+C+AT+LCover 5 to 1064063
Codes: +AT solution annealed, +A soft annealed, +PE peeled, +C cold drawn, +LC skin passed. Diameter ranges are over the first figure up to and including the second. No reduction of area is specified for +AT+C. For non-circular sections the properties are agreed between manufacturer and purchaser.
Source: IS 11169 (Part 2):2023, Table 11

Active IS 11169 (Part 2):2023 X02Cr18Ni9Cu3 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 11169 (Part 2):2023 X02Cr18Ni9Cu3 listings at this time.

Register for Alerts

Buyer RFQs for IS 11169 (Part 2):2023 X02Cr18Ni9Cu3

+ Post an RFQ for this grade

No open buyer requirements for IS 11169 (Part 2):2023 X02Cr18Ni9Cu3 at this time.

Register for Alerts