IS 11169 (Part 2) X02Cr18Ni9Cu3 vs EN 10088-1 X2CrNi18-9

Strong Match — 88.8% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr18Ni9Cu3 (IS 11169 (Part 2):2023) and EN 10088-1 X2CrNi18-9 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr18Ni9Cu3 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNi18-9 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X02Cr18Ni9Cu3 vs EN 10088-1 X2CrNi18-9 is a 88.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 88.8%.

Frequently Compared With IS 11169 (Part 2) X02Cr18Ni9Cu3:
EN 10088-1 1.4845 GOST 5632 12Kh13 GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
88.8%
MECHANICAL MATCH
No shared data
OVERALL
88.8%
Specifications
Property IS 11169 (Part 2) X02Cr18Ni9Cu3 EN 10088-1 X2CrNi18-9
Standard IS 11169 (Part 2):2023 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.030
Cr (%) 17.0-19.0 17.5-19.5
Cu (%) 3.00-4.00 Not specified
Mn (%) <=2.00 <=2.00
N (%) <=0.10 <=0.10
Ni (%) 8.5-10.5 8.0-10.5
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr18Ni9Cu3 EN 10088-1 X2CrNi18-9
Reduction of Area, solution annealed (+AT) >=68% (over 5 to 50 mm) Not specified
Tensile Strength, solution annealed (+AT) <=590 MPa (over 5 to 50 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr18Ni9Cu3
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
EN 10088-1 X2CrNi18-9
Not documented
Key Differences
Can IS 11169 (Part 2) X02Cr18Ni9Cu3 Be Substituted With EN 10088-1 X2CrNi18-9?
IS 11169 (Part 2) X02Cr18Ni9Cu3 and EN 10088-1 X2CrNi18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNi18-9 is often considered as a substitute for IS 11169 (Part 2) X02Cr18Ni9Cu3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr18Ni9Cu3
0 active listings and RFQs →
EN 10088-1 X2CrNi18-9
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr18Ni9Cu3 and EN 10088-1 X2CrNi18-9?
IS 11169 (Part 2) X02Cr18Ni9Cu3 specifies Cu which is not specified for EN 10088-1 X2CrNi18-9.
Can IS 11169 (Part 2) X02Cr18Ni9Cu3 be substituted with EN 10088-1 X2CrNi18-9?
IS 11169 (Part 2) X02Cr18Ni9Cu3 and EN 10088-1 X2CrNi18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNi18-9 is often considered as a substitute for IS 11169 (Part 2) X02Cr18Ni9Cu3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.