IS 11169 (Part 2) X02Ni18Cr16 vs ASTM A959 301LN

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Ni18Cr16 (IS 11169 (Part 2):2023) and ASTM A959 301LN (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Ni18Cr16 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while ASTM A959 301LN is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X02Ni18Cr16 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 301LN is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X02Ni18Cr16 vs ASTM A959 301LN is a 78.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 11169 (Part 2) X02Ni18Cr16:
EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
78.5%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 11169 (Part 2) X02Ni18Cr16 ASTM A959 301LN
Standard IS 11169 (Part 2):2023 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.030
Cr (%) 15.0-17.0 16.0-18.0
Mn (%) <=2.00 <=2.00
Ni (%) 17.0-19.0 5.0-8.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
N (%) Not specified 0.07-0.20
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Ni18Cr16 ASTM A959 301LN
Reduction of Area, cold drawn and solution annealed (+AT+C+AT) >=68% (0.8 to 5 mm) Not specified
Tensile Strength, cold drawn and solution annealed (+AT+C+AT) <=640 MPa (0.8 to 2 mm) / <=600 MPa (over 2 to 5 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Ni18Cr16
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
ASTM A959 301LN
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X02Ni18Cr16 Be Substituted With ASTM A959 301LN?
IS 11169 (Part 2) X02Ni18Cr16 and ASTM A959 301LN share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 2) X02Ni18Cr16
0 active listings and RFQs →
ASTM A959 301LN
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Ni18Cr16 and ASTM A959 301LN?
ASTM A959 301LN specifies N which is not specified for IS 11169 (Part 2) X02Ni18Cr16.
Can IS 11169 (Part 2) X02Ni18Cr16 be substituted with ASTM A959 301LN?
IS 11169 (Part 2) X02Ni18Cr16 and ASTM A959 301LN share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.