Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Ni18Cr16 (IS 11169 (Part 2):2023) and ASTM A959 XM-11 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Ni18Cr16 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while ASTM A959 XM-11 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X02Ni18Cr16 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 XM-11 is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X02Ni18Cr16 vs ASTM A959 XM-11 is a 72.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 11169 (Part 2) X02Ni18Cr16:
EN 10088-1 1.4401 ASTM A959 .- GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
72.2%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 11169 (Part 2) X02Ni18Cr16 ASTM A959 XM-11
Standard IS 11169 (Part 2):2023 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) <=0.04 <=0.04
Cr (%) 15.0-17.0 19.0-21.5
Mn (%) <=2.00 8.0-10.0
Ni (%) 17.0-19.0 5.5-7.5
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Si (%) <=1.00 <=1.00
N (%) Not specified 0.15-0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Ni18Cr16 ASTM A959 XM-11
Reduction of Area, cold drawn and solution annealed (+AT+C+AT) >=68% (0.8 to 5 mm) Not specified
Tensile Strength, cold drawn and solution annealed (+AT+C+AT) <=640 MPa (0.8 to 2 mm) / <=600 MPa (over 2 to 5 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Ni18Cr16
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
ASTM A959 XM-11
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X02Ni18Cr16 Be Substituted With ASTM A959 XM-11?
IS 11169 (Part 2) X02Ni18Cr16 and ASTM A959 XM-11 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 2) X02Ni18Cr16
0 active listings and RFQs →
ASTM A959 XM-11
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Ni18Cr16 and ASTM A959 XM-11?
ASTM A959 XM-11 specifies N which is not specified for IS 11169 (Part 2) X02Ni18Cr16.
Can IS 11169 (Part 2) X02Ni18Cr16 be substituted with ASTM A959 XM-11?
IS 11169 (Part 2) X02Ni18Cr16 and ASTM A959 XM-11 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.