IS 11169 (Part 2) X04Cr17 vs EN 10088-1 X10CrAlSi18

Close Alternative — 83.1% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X04Cr17 (IS 11169 (Part 2):2023) and EN 10088-1 X10CrAlSi18 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X04Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X10CrAlSi18 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X04Cr17 vs EN 10088-1 X10CrAlSi18 is a 83.1% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 83.1%.

Frequently Compared With IS 11169 (Part 2) X04Cr17:
IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoH GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
83.1%
MECHANICAL MATCH
No shared data
OVERALL
83.1%
Specifications
Property IS 11169 (Part 2) X04Cr17 EN 10088-1 X10CrAlSi18
Standard IS 11169 (Part 2):2023 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.12
Cr (%) 16.0-18.0 17.0-19.0
Mn (%) <=1.00 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.015
Si (%) <=1.00 0.70-1.40
Al (%) Not specified 0.70-1.20
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X04Cr17 EN 10088-1 X10CrAlSi18
Reduction of Area, soft annealed (+A) >=63% (over 5 to 25 mm) Not specified
Tensile Strength, soft annealed (+A) <=560 MPa (over 5 to 25 mm) Not specified
Typical Applications
IS 11169 (Part 2) X04Cr17
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
EN 10088-1 X10CrAlSi18
Not documented
Key Differences
Can IS 11169 (Part 2) X04Cr17 Be Substituted With EN 10088-1 X10CrAlSi18?
IS 11169 (Part 2) X04Cr17 and EN 10088-1 X10CrAlSi18 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 11169 (Part 2) X04Cr17
0 active listings and RFQs →
EN 10088-1 X10CrAlSi18
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X04Cr17 and EN 10088-1 X10CrAlSi18?
EN 10088-1 X10CrAlSi18 specifies Al which is not specified for IS 11169 (Part 2) X04Cr17.
Can IS 11169 (Part 2) X04Cr17 be substituted with EN 10088-1 X10CrAlSi18?
IS 11169 (Part 2) X04Cr17 and EN 10088-1 X10CrAlSi18 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.