Strong Match — 98.6% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr17 (IS 11169 (Part 2):2023) and EN 10088-1 X6Cr17 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X6Cr17 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 11169 (Part 2) X04Cr17 vs EN 10088-1 X6Cr17 is a 98.6% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 98.6%.
Frequently Compared With IS 11169 (Part 2) X04Cr17:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr17
EN 10088-1 X6Cr17
Reduction of Area, soft annealed (+A)
>=63% (over 5 to 25 mm)
Not specified
Tensile Strength, soft annealed (+A)
<=560 MPa (over 5 to 25 mm)
Not specified
Typical Applications
IS 11169 (Part 2) X04Cr17
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
EN 10088-1 X6Cr17
Not documented
Can IS 11169 (Part 2) X04Cr17 Be Substituted With EN 10088-1 X6Cr17?
IS 11169 (Part 2) X04Cr17 and EN 10088-1 X6Cr17 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X6Cr17 is often considered as a substitute for IS 11169 (Part 2) X04Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 11169 (Part 2) X04Cr17 and EN 10088-1 X6Cr17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X04Cr17 be substituted with EN 10088-1 X6Cr17?
IS 11169 (Part 2) X04Cr17 and EN 10088-1 X6Cr17 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X6Cr17 is often considered as a substitute for IS 11169 (Part 2) X04Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.