IS 1570 (Part 2/Sec 1) 10C4 vs IS 4432 C10

Strong Match — 95.8% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 2/Sec 1) 10C4 (IS 1570 (Part 2/Sec 1):1979) and IS 4432 C10 (IS 4432:1967) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 2/Sec 1) 10C4 is typically used for wire for wood screws, welding electrode core wire and case hardened parts (the standard links this grade to is 1812, is 2879, is 4432), while IS 4432 C10 is commonly used for bolts, nuts, shafts, pins, general engineering parts, structural components, welded assemblies. IS 1570 (Part 2/Sec 1) 10C4 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4432 C10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 2/Sec 1) 10C4 vs IS 4432 C10 is a 93.7% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 95.8%.

Frequently Compared With IS 1570 (Part 2/Sec 1) 10C4:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
93.7%
MECHANICAL MATCH
100%
OVERALL
95.8%
Specifications
Property IS 1570 (Part 2/Sec 1) 10C4 IS 4432 C10
Standard IS 1570 (Part 2/Sec 1):1979 IS 4432:1967
Category Carbon Steel Carbon Steel
C (%) <=0.15 <=0.15
Mn (%) 0.30-0.60 0.30-0.60
Si (%) Not specified 0.15-0.35
S (%) Not specified <=0.045
P (%) Not specified <=0.045
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 2/Sec 1) 10C4 IS 4432 C10
Tensile Strength 340-420 MPa 340-420 MPa
Elongation >=26% >=26%
Yield Strength Not specified >=187 MPa
Hardness Not specified <=120 HB
Typical Applications
IS 1570 (Part 2/Sec 1) 10C4
Wire for wood screws, welding electrode core wire and case hardened parts (the standard links this grade to IS 1812, IS 2879, IS 4432)
IS 4432 C10
bolts, nuts, shafts, pins, general engineering parts, structural components, welded assemblies
Key Differences
Can IS 1570 (Part 2/Sec 1) 10C4 Be Substituted With IS 4432 C10?
IS 1570 (Part 2/Sec 1) 10C4 and IS 4432 C10 overlap closely enough on chemistry and mechanical properties that IS 4432 C10 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 10C4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 1570 (Part 2/Sec 1) 10C4
No active listings currently.
IS 4432 C10
Round Bar → (5 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5000–6900 mm (196.85–271.65 in)
On M-EX Right Now
IS 1570 (Part 2/Sec 1) 10C4
0 active listings and RFQs →
IS 4432 C10
5 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 2/Sec 1) 10C4 and IS 4432 C10?
IS 4432 C10 specifies Si, S, P which are not specified for IS 1570 (Part 2/Sec 1) 10C4.
Can IS 1570 (Part 2/Sec 1) 10C4 be substituted with IS 4432 C10?
IS 1570 (Part 2/Sec 1) 10C4 and IS 4432 C10 overlap closely enough on chemistry and mechanical properties that IS 4432 C10 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 10C4 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.