IS 1570 (Part 2/Sec 1) 35C8 vs BS 970 (Part 1) 080H36

Strong Match — 96% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 2/Sec 1) 35C8 (IS 1570 (Part 2/Sec 1):1979) and BS 970 (Part 1) 080H36 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 2/Sec 1) 35C8 is typically used for billets and bars for forgings, carbon steel forgings, flame and induction hardened parts and hardened and tempered parts (the standard links this grade to is 1875, is 2004, is 3930, is 5517), while BS 970 (Part 1) 080H36 is commonly used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6.. IS 1570 (Part 2/Sec 1) 35C8 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 080H36 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 2/Sec 1) 35C8 vs BS 970 (Part 1) 080H36 is a 96% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 96%.

Frequently Compared With IS 1570 (Part 2/Sec 1) 35C8:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045A10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
96%
MECHANICAL MATCH
No shared data
OVERALL
96%
Specifications
Property IS 1570 (Part 2/Sec 1) 35C8 BS 970 (Part 1) 080H36
Standard IS 1570 (Part 2/Sec 1):1979 BS 970 (Part 1):1983
Category Carbon Steel Carbon Steel
C (%) 0.30-0.40 0.33-0.40
Mn (%) 0.60-0.90 0.60-1.00
P (%) Not specified <=0.050
S (%) Not specified <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 2/Sec 1) 35C8 BS 970 (Part 1) 080H36
Tensile Strength 550-650 MPa Not specified
Elongation >=20% Not specified
Typical Applications
IS 1570 (Part 2/Sec 1) 35C8
Billets and bars for forgings, carbon steel forgings, flame and induction hardened parts and hardened and tempered parts (the standard links this grade to IS 1875, IS 2004, IS 3930, IS 5517)
BS 970 (Part 1) 080H36
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Key Differences
Can IS 1570 (Part 2/Sec 1) 35C8 Be Substituted With BS 970 (Part 1) 080H36?
IS 1570 (Part 2/Sec 1) 35C8 and BS 970 (Part 1) 080H36 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 080H36 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 35C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 2/Sec 1) 35C8
0 active listings and RFQs →
BS 970 (Part 1) 080H36
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 2/Sec 1) 35C8 and BS 970 (Part 1) 080H36?
BS 970 (Part 1) 080H36 specifies P, S which are not specified for IS 1570 (Part 2/Sec 1) 35C8.
Can IS 1570 (Part 2/Sec 1) 35C8 be substituted with BS 970 (Part 1) 080H36?
IS 1570 (Part 2/Sec 1) 35C8 and BS 970 (Part 1) 080H36 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 080H36 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 35C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.