IS 1570 (Part 5) X04Cr19Ni13Mo3 vs IS 1570 (Part 5) X04Cr17Ni12Mo2

Close Alternative — 78.3% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X04Cr19Ni13Mo3 (IS 1570 (Part 5):1985) and IS 1570 (Part 5) X04Cr17Ni12Mo2 (IS 1570 (Part 5):1985) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X04Cr19Ni13Mo3 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 5) X04Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 5) X04Cr19Ni13Mo3 vs IS 1570 (Part 5) X04Cr17Ni12Mo2 is a 80% match. As per mechanical properties, the match is 75%. Combined, this makes them a close alternative overall at 78.3%.

Frequently Compared With IS 1570 (Part 5) X04Cr19Ni13Mo3:
GOST 5632 08X18H10 EN 10088-1 1.4845 IS 1570 (Part 7) 11Cr17Ni13W3TiH GOST 5632 12Kh13 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr13H IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
80%
MECHANICAL MATCH
75%
OVERALL
78.3%
Specifications
Property IS 1570 (Part 5) X04Cr19Ni13Mo3 IS 1570 (Part 5) X04Cr17Ni12Mo2
Standard IS 1570 (Part 5):1985 IS 1570 (Part 5):1985
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Si (%) <=1.0 <=1.0
Mn (%) <=2.0 <=2.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.030
Cr (%) 18.0-20.0 16.0-18.0
Ni (%) 11.0-15.0 10.0-14.0
Mo (%) 3.0-4.0 2.0-3.0
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X04Cr19Ni13Mo3 IS 1570 (Part 5) X04Cr17Ni12Mo2
Tensile Strength >=515 MPa >=515 MPa
Yield Strength >=205 MPa (0.2 % proof stress) >=205 MPa (0.2 % proof stress)
Elongation >=35% (50 mm) >=40% (50 mm)
Hardness <=217 HB; <=95 HRB <=217 HB; <=95 HRB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Can IS 1570 (Part 5) X04Cr19Ni13Mo3 Be Substituted With IS 1570 (Part 5) X04Cr17Ni12Mo2?
IS 1570 (Part 5) X04Cr19Ni13Mo3 and IS 1570 (Part 5) X04Cr17Ni12Mo2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 5) X04Cr19Ni13Mo3
0 active listings and RFQs →
IS 1570 (Part 5) X04Cr17Ni12Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X04Cr19Ni13Mo3 and IS 1570 (Part 5) X04Cr17Ni12Mo2?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X04Cr19Ni13Mo3 be substituted with IS 1570 (Part 5) X04Cr17Ni12Mo2?
IS 1570 (Part 5) X04Cr19Ni13Mo3 and IS 1570 (Part 5) X04Cr17Ni12Mo2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.