Strong Match — 98.1% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X07Cr17 (IS 1570 (Part 5):1985) and ASTM A240/A240M S43000 (ASTM A240/A240M:2025) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A240/A240M S43000 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X07Cr17 vs ASTM A240/A240M S43000 is a 97.2% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 98.1%.

Frequently Compared With IS 1570 (Part 5) X07Cr17:
EN 10088-1 1.4006 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 GOST 5632 06Kh23N28 GOST 5632 12Kh13 ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
97.2%
MECHANICAL MATCH
100%
OVERALL
98.1%
Specifications
Property IS 1570 (Part 5) X07Cr17 ASTM A240/A240M S43000
Standard IS 1570 (Part 5):1985 ASTM A240/A240M:2025
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.12
Si (%) <=1.0 <=1.00
Mn (%) <=1.0 <=1.00
P (%) <=0.040 <=0.040
S (%) <=0.030 <=0.030
Cr (%) 16.0-18.0 16.0-18.0
Ni (%) <=0.5 <=0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X07Cr17 ASTM A240/A240M S43000
Tensile Strength >=450 MPa >=450 MPa
Yield Strength >=205 MPa (0.2 % proof stress) >=205 MPa
Elongation >=22.0% (50 mm) >=22%
Hardness <=183 HB; <=88 HRB <=183 HB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Plate, sheet and strip; yield by 0.2 percent offset
Typical Applications
IS 1570 (Part 5) X07Cr17
Not documented
ASTM A240/A240M S43000
Pressure vessels and general applications (plate, sheet and strip)
Can IS 1570 (Part 5) X07Cr17 Be Substituted With ASTM A240/A240M S43000?
IS 1570 (Part 5) X07Cr17 and ASTM A240/A240M S43000 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S43000 is often considered as a substitute for IS 1570 (Part 5) X07Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 5) X07Cr17
0 active listings and RFQs →
ASTM A240/A240M S43000
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X07Cr17 and ASTM A240/A240M S43000?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X07Cr17 be substituted with ASTM A240/A240M S43000?
IS 1570 (Part 5) X07Cr17 and ASTM A240/A240M S43000 overlap closely enough on chemistry and mechanical properties that ASTM A240/A240M S43000 is often considered as a substitute for IS 1570 (Part 5) X07Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.