Strong Match — 93.5% match
based on chemical composition and mechanical property overlap.
IS 1570 (Part 5) X07Cr17 (IS 1570 (Part 5):1985) and JIS G4304 SUS429 (JIS G4304:2021) are both steel grades.
Both fall under the Stainless Steel category.
IS 1570 (Part 5) X07Cr17 is defined under Bureau of Indian Standards (IS), originating from India, while JIS G4304 SUS429 is defined under Japanese Industrial Standards (JIS), originating from Japan.
As per chemical composition, IS 1570 (Part 5) X07Cr17 vs JIS G4304 SUS429 is a 90.3% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 93.5%.
Frequently Compared With IS 1570 (Part 5) X07Cr17:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 1570 (Part 5) X07Cr17
JIS G4304 SUS429
Tensile Strength
>=450 MPa
>=450 MPa
Yield Strength
>=205 MPa (0.2 % proof stress)
>=205 MPa
Elongation
>=22.0% (50 mm)
>=22%
Hardness
<=183 HB; <=88 HRB
<=183 HB
Condition
Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Annealed plate and strip; proof strength applies only when specified by the purchaser
Typical Applications
IS 1570 (Part 5) X07Cr17
Not documented
JIS G4304 SUS429
Hot-rolled stainless steel plates and strips
Can IS 1570 (Part 5) X07Cr17 Be Substituted With JIS G4304 SUS429?
IS 1570 (Part 5) X07Cr17 and JIS G4304 SUS429 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS429 is often considered as a substitute for IS 1570 (Part 5) X07Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 1570 (Part 5) X07Cr17 and JIS G4304 SUS429?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X07Cr17 be substituted with JIS G4304 SUS429?
IS 1570 (Part 5) X07Cr17 and JIS G4304 SUS429 overlap closely enough on chemistry and mechanical properties that JIS G4304 SUS429 is often considered as a substitute for IS 1570 (Part 5) X07Cr17 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.