IS 1570 (Part 5):1985 X07Cr17Mn12Ni4 Steel: Specifications & Listings

IS 1570 (Part 5):1985 X07Cr17Mn12Ni4: X07Cr17Mn12Ni4: high alloy, stainless or heat-resisting steel. Specified in IS 1570 (Part 5):1985.

Category: Stainless Steel
Grade Details
GradeIS 1570 (Part 5):1985 X07Cr17Mn12Ni4
Standard IS 1570 (Part 5):1985
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 6911 X07Cr17Mn12Ni4 IS 6911:1992 India No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 202 ASTM A959:2011 Close Alternative
EN 10088-1 X12CrMnNiN18-9-5 EN 10088-1:2014 Close Alternative
EN 10088-1 X12CrMnNiN18-9-5 EN 10088-1:2023 Close Alternative
ASTM A959 XM-28 ASTM A959:2011 Close Alternative
EN 10088-1 X13CrMnNiN18-13-2 EN 10088-1:2014 Close Alternative
EN 10088-1 X13CrMnNiN18-13-2 EN 10088-1:2023 Close Alternative
EN 10088-1 X9CrMnNiCu17-8-5-2 EN 10088-1:2014 Close Alternative
EN 10088-1 X9CrMnNiCu17-8-5-2 EN 10088-1:2023 Close Alternative
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn P S Cr Ni N
<=0.12 <=1.0 10.0-14.0 <=0.045 <=0.030 16.0-18.0 3.5-5.5 <=0.25
Mechanical Properties
Tensile Strength >=550 MPa
Yield Strength >=250 MPa (0.2 % proof stress)
Elongation >=45% (50 mm)
Hardness <=217 HB; <=88 HRB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2)

More data from IS 1570 (Part 5):1985

From the standard
Annealed, quenched or solution treated plates, sheets and strips 5 properties
Tensile strength, min
550 MPa
0.2 % proof stress, min
250 MPa
Elongation in 50 mm, min
45%
Brinell hardness, max
217 HB
Rockwell B hardness, max
88 HRB
Source: IS 1570 (Part 5):1985, Table 2
Recommended heat treatment 2 entries
Solution treatment (softening) temperature
1000 to 1150 deg C
Solution treatment quenching medium
water, oil, air
A annealing, S softening, ST solution treatment, Q quenching, T tempering, P patenting.
Source: IS 1570 (Part 5):1985, Table 7

Active IS 1570 (Part 5):1985 X07Cr17Mn12Ni4 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 1570 (Part 5):1985 X07Cr17Mn12Ni4 listings at this time.

Register for Alerts

Buyer RFQs for IS 1570 (Part 5):1985 X07Cr17Mn12Ni4

+ Post an RFQ for this grade

No open buyer requirements for IS 1570 (Part 5):1985 X07Cr17Mn12Ni4 at this time.

Register for Alerts