IS 1570 (Part 5) X07Cr17Mn12Ni4 vs EN 10088-1 X9CrMnNiCu17-8-5-2

Close Alternative — 77.7% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X07Cr17Mn12Ni4 (IS 1570 (Part 5):1985) and EN 10088-1 X9CrMnNiCu17-8-5-2 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X07Cr17Mn12Ni4 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X9CrMnNiCu17-8-5-2 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X07Cr17Mn12Ni4 vs EN 10088-1 X9CrMnNiCu17-8-5-2 is a 77.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 77.7%.

Frequently Compared With IS 1570 (Part 5) X07Cr17Mn12Ni4:
ASTM A959 202 ASTM A959 201 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo
Match Breakdown
CHEMISTRY MATCH
77.7%
MECHANICAL MATCH
No shared data
OVERALL
77.7%
Specifications
Property IS 1570 (Part 5) X07Cr17Mn12Ni4 EN 10088-1 X9CrMnNiCu17-8-5-2
Standard IS 1570 (Part 5):1985 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.12 <=0.10
Si (%) <=1.0 <=1.00
Mn (%) 10.0-14.0 5.5-9.5
P (%) <=0.045 <=0.070
S (%) <=0.030 <=0.010
Cr (%) 16.0-18.0 16.5-18.5
Ni (%) 3.5-5.5 4.5-5.5
N (%) <=0.25 <=0.15
Cu (%) Not specified 1.00-2.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X07Cr17Mn12Ni4 EN 10088-1 X9CrMnNiCu17-8-5-2
Tensile Strength >=550 MPa Not specified
Yield Strength >=250 MPa (0.2 % proof stress) Not specified
Elongation >=45% (50 mm) Not specified
Hardness <=217 HB; <=88 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Key Differences
Can IS 1570 (Part 5) X07Cr17Mn12Ni4 Be Substituted With EN 10088-1 X9CrMnNiCu17-8-5-2?
IS 1570 (Part 5) X07Cr17Mn12Ni4 and EN 10088-1 X9CrMnNiCu17-8-5-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 5) X07Cr17Mn12Ni4
0 active listings and RFQs →
EN 10088-1 X9CrMnNiCu17-8-5-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X07Cr17Mn12Ni4 and EN 10088-1 X9CrMnNiCu17-8-5-2?
EN 10088-1 X9CrMnNiCu17-8-5-2 specifies Cu which is not specified for IS 1570 (Part 5) X07Cr17Mn12Ni4.
Can IS 1570 (Part 5) X07Cr17Mn12Ni4 be substituted with EN 10088-1 X9CrMnNiCu17-8-5-2?
IS 1570 (Part 5) X07Cr17Mn12Ni4 and EN 10088-1 X9CrMnNiCu17-8-5-2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.