IS 1570 (Part 5) X07Cr17Mn12Ni4 vs EN 10088-1 1.4301

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X07Cr17Mn12Ni4 (IS 1570 (Part 5):1985) and EN 10088-1 1.4301 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X07Cr17Mn12Ni4 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4301 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X07Cr17Mn12Ni4 vs EN 10088-1 1.4301 is a 63% match. As per mechanical properties, the match is 25%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X07Cr17Mn12Ni4:
ASTM A959 202 ASTM A959 201 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4401 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4845 GOST 5632 06Kh23N28 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
63%
MECHANICAL MATCH
25%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X07Cr17Mn12Ni4 EN 10088-1 1.4301
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.12 ≤0.07
Si (%) <=1.0 ≤1.00
Mn (%) 10.0-14.0 ≤2.00
P (%) <=0.045 ≤0.045
S (%) <=0.030 ≤0.030
Cr (%) 16.0-18.0 17.5–19.5
Ni (%) 3.5-5.5 8.0–10.5
N (%) <=0.25 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X07Cr17Mn12Ni4 EN 10088-1 1.4301
Tensile Strength >=550 MPa ≥520 MPa
Yield Strength >=250 MPa (0.2 % proof stress) ≥210 MPa
Elongation >=45% (50 mm) ≥45%
Hardness <=217 HB; <=88 HRB ≤215 HB
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X07Cr17Mn12Ni4
Not documented
EN 10088-1 1.4301
Food equipment, chemical vessels, architectural, kitchenware
Key Differences
Can IS 1570 (Part 5) X07Cr17Mn12Ni4 Be Substituted With EN 10088-1 1.4301?
IS 1570 (Part 5) X07Cr17Mn12Ni4 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X07Cr17Mn12Ni4
No active listings currently.
EN 10088-1 1.4301
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–3300 mm (98.43–129.92 in)
On M-EX Right Now
IS 1570 (Part 5) X07Cr17Mn12Ni4
0 active listings and RFQs →
EN 10088-1 1.4301
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X07Cr17Mn12Ni4 and EN 10088-1 1.4301?
IS 1570 (Part 5) X07Cr17Mn12Ni4 specifies N which is not specified for EN 10088-1 1.4301.
Can IS 1570 (Part 5) X07Cr17Mn12Ni4 be substituted with EN 10088-1 1.4301?
IS 1570 (Part 5) X07Cr17Mn12Ni4 and EN 10088-1 1.4301 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.