IS 1570 (Part 5) X07Cr17Mn12Ni4 vs GOST 5632 08X18H10

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X07Cr17Mn12Ni4 (IS 1570 (Part 5):1985) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X07Cr17Mn12Ni4 is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 1570 (Part 5) X07Cr17Mn12Ni4 vs GOST 5632 08X18H10 is a 64.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X07Cr17Mn12Ni4:
ASTM A959 202 ASTM A959 201 EN 10088-1 1.4401 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 GOST 5632 06Kh23N28 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
64.6%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X07Cr17Mn12Ni4 GOST 5632 08X18H10
Standard IS 1570 (Part 5):1985 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.12 ≤0.08
Si (%) <=1.0 ≤0.80
Mn (%) 10.0-14.0 ≤2.00
P (%) <=0.045 ≤0.035
S (%) <=0.030 ≤0.020
Cr (%) 16.0-18.0 17.0–19.0
Ni (%) 3.5-5.5 9.0–11.0
N (%) <=0.25 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X07Cr17Mn12Ni4 GOST 5632 08X18H10
Tensile Strength >=550 MPa ≥520 MPa
Yield Strength >=250 MPa (0.2 % proof stress) ≥205 MPa
Elongation >=45% (50 mm) ≥40%
Hardness <=217 HB; <=88 HRB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X07Cr17Mn12Ni4
Not documented
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
Can IS 1570 (Part 5) X07Cr17Mn12Ni4 Be Substituted With GOST 5632 08X18H10?
IS 1570 (Part 5) X07Cr17Mn12Ni4 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X07Cr17Mn12Ni4
No active listings currently.
GOST 5632 08X18H10
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2500–2700 mm (98.43–106.3 in)
On M-EX Right Now
IS 1570 (Part 5) X07Cr17Mn12Ni4
0 active listings and RFQs →
GOST 5632 08X18H10
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X07Cr17Mn12Ni4 and GOST 5632 08X18H10?
IS 1570 (Part 5) X07Cr17Mn12Ni4 specifies N which is not specified for GOST 5632 08X18H10.
Can IS 1570 (Part 5) X07Cr17Mn12Ni4 be substituted with GOST 5632 08X18H10?
IS 1570 (Part 5) X07Cr17Mn12Ni4 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.