IS 1570 (Part 5) X108Cr17Mo vs ASTM A959 S44025

Close Alternative — 80.8% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X108Cr17Mo (IS 1570 (Part 5):1985) and ASTM A959 S44025 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X108Cr17Mo is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 S44025 is defined under ASTM International, originating from United States.

As per chemical composition, IS 1570 (Part 5) X108Cr17Mo vs ASTM A959 S44025 is a 80.8% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 80.8%.

Frequently Compared With IS 1570 (Part 5) X108Cr17Mo:
GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr12MoVH EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 12Cr13H GOST 5632 12Kh13
Match Breakdown
CHEMISTRY MATCH
80.8%
MECHANICAL MATCH
No shared data
OVERALL
80.8%
Specifications
Property IS 1570 (Part 5) X108Cr17Mo ASTM A959 S44025
Standard IS 1570 (Part 5):1985 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.95-1.20 0.95-1.10
Si (%) <=1.0 0.30-1.00
Mn (%) <=1.0 0.30-1.00
P (%) <=0.045 <=0.025
S (%) <=0.030 <=0.025
Cr (%) 16.0-18.0 16.0-18.0
Ni (%) <=0.50 <=0.75
Mo (%) <=0.75 0.40-0.65
Cu (%) Not specified <=0.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X108Cr17Mo ASTM A959 S44025
Hardness <=269 HB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Typical Applications
IS 1570 (Part 5) X108Cr17Mo
Not documented
ASTM A959 S44025
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 1570 (Part 5) X108Cr17Mo Be Substituted With ASTM A959 S44025?
IS 1570 (Part 5) X108Cr17Mo and ASTM A959 S44025 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 5) X108Cr17Mo
0 active listings and RFQs →
ASTM A959 S44025
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X108Cr17Mo and ASTM A959 S44025?
ASTM A959 S44025 specifies Cu which is not specified for IS 1570 (Part 5) X108Cr17Mo.
Can IS 1570 (Part 5) X108Cr17Mo be substituted with ASTM A959 S44025?
IS 1570 (Part 5) X108Cr17Mo and ASTM A959 S44025 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.