IS 1570 (Part 5) X15Cr25N vs EN 10088-1 1.4006

Minimal Match — 46.5% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X15Cr25N (IS 1570 (Part 5):1985) and EN 10088-1 1.4006 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X15Cr25N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 1.4006 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X15Cr25N vs EN 10088-1 1.4006 is a 69.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 46.5%.

Frequently Compared With IS 1570 (Part 5) X15Cr25N:
GOST 5632 12Kh13 GOST 5632 06Kh23N28 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
69.8%
MECHANICAL MATCH
0%
OVERALL
46.5%
Specifications
Property IS 1570 (Part 5) X15Cr25N EN 10088-1 1.4006
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.20 0.08–0.15
Si (%) <=1.0 ≤1.00
Mn (%) <=1.5 ≤1.50
P (%) <=0.045 Not specified
S (%) <=0.030 Not specified
Cr (%) 23.0-27.0 11.5–13.5
N (%) <=0.25 Not specified
Ni (%) Not specified ≤0.75
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X15Cr25N EN 10088-1 1.4006
Tensile Strength >=515 MPa ≥540 MPa (annealed)
Yield Strength >=275 MPa (0.2 % proof stress) Not specified
Elongation >=20% (50 mm) ≥18%
Hardness <=217 HB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 1570 (Part 5) X15Cr25N
Not documented
EN 10088-1 1.4006
Cutlery, turbine blades, fasteners, surgical instruments
Key Differences
Can IS 1570 (Part 5) X15Cr25N Be Substituted With EN 10088-1 1.4006?
IS 1570 (Part 5) X15Cr25N and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 5) X15Cr25N
No active listings currently.
EN 10088-1 1.4006
Sheet → (3 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 1570 (Part 5) X15Cr25N
0 active listings and RFQs →
EN 10088-1 1.4006
3 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X15Cr25N and EN 10088-1 1.4006?
IS 1570 (Part 5) X15Cr25N specifies P, S, N which are not specified for EN 10088-1 1.4006. EN 10088-1 1.4006 specifies Ni which is not specified for IS 1570 (Part 5) X15Cr25N.
Can IS 1570 (Part 5) X15Cr25N be substituted with EN 10088-1 1.4006?
IS 1570 (Part 5) X15Cr25N and EN 10088-1 1.4006 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.