IS 1570 (Part 5) X15Cr25N vs IS 1570 (Part 7) 12Cr12MoVH

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X15Cr25N (IS 1570 (Part 5):1985) and IS 1570 (Part 7) 12Cr12MoVH (IS 1570 (Part 7):1992) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X15Cr25N is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 7) 12Cr12MoVH is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 5) X15Cr25N vs IS 1570 (Part 7) 12Cr12MoVH is a 54.2% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 1570 (Part 5) X15Cr25N:
GOST 5632 06Kh23N28 GOST 5632 12Kh13 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
54.2%
MECHANICAL MATCH
0%
OVERALL
35%
Specifications
Property IS 1570 (Part 5) X15Cr25N IS 1570 (Part 7) 12Cr12MoVH
Standard IS 1570 (Part 5):1985 IS 1570 (Part 7):1992
Category Stainless Steel Stainless Steel
C (%) <=0.20 0.08-0.16
Si (%) <=1.0 <=0.60
Mn (%) <=1.5 0.40-1.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.035
Cr (%) 23.0-27.0 11.5-13.00
N (%) <=0.25 Not specified
Ni (%) Not specified <=1.0
Mo (%) Not specified 0.40-0.80
V (%) Not specified 0.10-0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X15Cr25N IS 1570 (Part 7) 12Cr12MoVH
Tensile Strength >=515 MPa 770-930 MPa
Yield Strength >=275 MPa (0.2 % proof stress) >=585 MPa (0.2 % proof stress)
Elongation >=20% (50 mm) >=15%
Hardness <=217 HB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Bars, forgings, Q+T, thickness up to 150 (first row of Table 3)
Typical Applications
IS 1570 (Part 5) X15Cr25N
Not documented
IS 1570 (Part 7) 12Cr12MoVH
Boilers, pressure vessels, steam turbines, steam and water piping and other power plant equipment working at elevated temperature
Key Differences
Can IS 1570 (Part 5) X15Cr25N Be Substituted With IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 5) X15Cr25N and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 5) X15Cr25N
0 active listings and RFQs →
IS 1570 (Part 7) 12Cr12MoVH
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X15Cr25N and IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 5) X15Cr25N specifies N which is not specified for IS 1570 (Part 7) 12Cr12MoVH. IS 1570 (Part 7) 12Cr12MoVH specifies Ni, Mo, V which are not specified for IS 1570 (Part 5) X15Cr25N.
Can IS 1570 (Part 5) X15Cr25N be substituted with IS 1570 (Part 7) 12Cr12MoVH?
IS 1570 (Part 5) X15Cr25N and IS 1570 (Part 7) 12Cr12MoVH share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.