Close Alternative — 79.4% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 5) X15Cr25N (IS 1570 (Part 5):1985) and EN 10088-1 X10CrAlSi25 (EN 10088-1:2014) are both steel grades. Both fall under the Stainless Steel category. IS 1570 (Part 5) X15Cr25N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X10CrAlSi25 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 5) X15Cr25N vs EN 10088-1 X10CrAlSi25 is a 79.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 79.4%.

Frequently Compared With IS 1570 (Part 5) X15Cr25N:
GOST 5632 06Kh23N28 GOST 5632 12Kh13 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 IS 1570 (Part 7) 12Cr12Ni2Mo ASTM A959 .- IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
79.4%
MECHANICAL MATCH
No shared data
OVERALL
79.4%
Specifications
Property IS 1570 (Part 5) X15Cr25N EN 10088-1 X10CrAlSi25
Standard IS 1570 (Part 5):1985 EN 10088-1:2014
Category Stainless Steel Stainless Steel
C (%) <=0.20 <=0.12
Si (%) <=1.0 0.70-1.40
Mn (%) <=1.5 <=1.00
P (%) <=0.045 <=0.040
S (%) <=0.030 <=0.015
Cr (%) 23.0-27.0 23.0-26.0
N (%) <=0.25 Not specified
Al (%) Not specified 1.20-1.70
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 5) X15Cr25N EN 10088-1 X10CrAlSi25
Tensile Strength >=515 MPa Not specified
Yield Strength >=275 MPa (0.2 % proof stress) Not specified
Elongation >=20% (50 mm) Not specified
Hardness <=217 HB Not specified
Condition Annealed, quenched or solution treated plates, sheets and strips (Table 2) Not specified
Key Differences
Can IS 1570 (Part 5) X15Cr25N Be Substituted With EN 10088-1 X10CrAlSi25?
IS 1570 (Part 5) X15Cr25N and EN 10088-1 X10CrAlSi25 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 5) X15Cr25N
0 active listings and RFQs →
EN 10088-1 X10CrAlSi25
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 5) X15Cr25N and EN 10088-1 X10CrAlSi25?
IS 1570 (Part 5) X15Cr25N specifies N which is not specified for EN 10088-1 X10CrAlSi25. EN 10088-1 X10CrAlSi25 specifies Al which is not specified for IS 1570 (Part 5) X15Cr25N.
Can IS 1570 (Part 5) X15Cr25N be substituted with EN 10088-1 X10CrAlSi25?
IS 1570 (Part 5) X15Cr25N and EN 10088-1 X10CrAlSi25 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.