Close Alternative — 79.9% match
based on chemical composition and mechanical property overlap.
IS 1570 (Part 5) X15Cr25N (IS 1570 (Part 5):1985) and EN 10088-1 X18CrN28 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 1570 (Part 5) X15Cr25N is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X18CrN28 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 1570 (Part 5) X15Cr25N vs EN 10088-1 X18CrN28 is a 79.9% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 79.9%.
Frequently Compared With IS 1570 (Part 5) X15Cr25N:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 1570 (Part 5) X15Cr25N
EN 10088-1 X18CrN28
Tensile Strength
>=515 MPa
Not specified
Yield Strength
>=275 MPa (0.2 % proof stress)
Not specified
Elongation
>=20% (50 mm)
Not specified
Hardness
<=217 HB
Not specified
Condition
Annealed, quenched or solution treated plates, sheets and strips (Table 2)
Not specified
Can IS 1570 (Part 5) X15Cr25N Be Substituted With EN 10088-1 X18CrN28?
IS 1570 (Part 5) X15Cr25N and EN 10088-1 X18CrN28 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between IS 1570 (Part 5) X15Cr25N and EN 10088-1 X18CrN28?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 5) X15Cr25N be substituted with EN 10088-1 X18CrN28?
IS 1570 (Part 5) X15Cr25N and EN 10088-1 X18CrN28 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.